Examination of Hardened Cement Paste

Structure and Physical Properties of Hardened Portland Cement Paste

Determining the water - cement ratio , cement content , water content and degree 1 of hydration of hardened cement paste : Method development and validation on 2 paste samples

7 We propose a new method to estimate the initial cement content, water content and free water/cement ratio (w/c) 8 of hardened cement-based materials made with Portland cements that have unknown mixture proportions and 9 degree of hydration. This method first quantifies the composition of the hardened cement paste, i.e. the 10 volumetric fractions of capillary pores, hydration products and unr...

ESTIMATING THE 95 th PERCENTILE OF THE PASTE- VOID SPACING DISTRIBUTION IN HARDENED CEMENT PASTE CONTAINING AIR ENTRAINMENT

The spacing equations of Powers, Philleo, and Pleau and Pigeon are used to estimate the uniform thickness of paste surrounding entrained air voids that is required to encompass 95 % of the air-paste system. Spacing equation accuracy is determined by comparison to the numerically exact result of Lu and Torquato. The air void system is approximated by spheres with radii from a lognormal distribut...

The Surface Area of Hardened Cement Paste as Measured by Various Techniques

Hydrated cement paste has a high specific surface area due almost entirely to the calcium-silicate-hydrate reaction product. The surface area of cement paste is closely related to many crucial properties, including strength and permeability, and is therefore a useful predictive measurement. It is also a useful parameter for studying the nature of the calcium-silicate-hydrate gel itself. Unfortu...

Influence of hardened cement paste content on the water absorption of fine recycled concrete aggregates

Influence of hardened cement paste content on the water absorption of fine recycled concrete aggregates Zengfeng Zhao a b , Sébastien Remond a b , Denis Damidot a b & Weiya Xu c a Université Lille Nord de France , Lille , France b Civil and Environmental Engineering Department , Mines Douai, LGCgE GCE , Douai , France c Geotechnical Research Institute , Hohai University , Nanjing , China Publis...