Evaluation of Elevated-Temperature Crack Growth in Ceramics under Static and Cyclic Loads.
نویسندگان
چکیده
منابع مشابه
High-Temperature Cyclic Fatigue-Crack Growth in Monolithic Ti3SiC2 Ceramics
identical slip planes) and walls or kink boundaries. Thus, in addition to regular slip, mechanisms for ambient temperature The cyclic fatigue behavior of reactive hot-pressed Ti3SiCz plastic deformation in Ti3SiCz are thought to involve the ceramics are examined at temperatures from ambient to 1200°C readjustment of local stress and strain fields from kink band with the objective of characteriz...
متن کاملHigh-temperature Cyclic Fatigue-crack Growth Behavior in an in Situ Toughened Silicon Carbide
The growth of fatigue cracks at elevated temperatures (25–1300°C) is examined under cyclic loading in an in situ toughened, monolithic silicon carbide with Al-B-C additions (termed ABC–SiC), with specific emphasis on the roles of temperature, load ratio, cyclic frequency, and loading mode (static vs. cyclic). Extensive crack-growth data are presented, based on measurements from an electrical ...
متن کاملCrack Propagation Calculations for Optical Fibers under Static Bending and Tensile Loads Using Continuum Damage Mechanics
Static fatigue behavior is the main failure mode of optical fibers applied in sensors. In this paper, a computational framework based on continuum damage mechanics (CDM) is presented to calculate the crack propagation process and failure time of optical fibers subjected to static bending and tensile loads. For this purpose, the static fatigue crack propagation in the glass core of the optical f...
متن کاملMultiscale behavior of crack initiation and growth in piezoelectric ceramics
The multiscale nature of cracking in ferroelectric ceramics is explored in relation to the crack growth enhancement and retardation behavior when the direction of applied electric ®eld is reversed with reference to that of poling. An a priori knowledge of the prevailing fracture behavior is invoked for the energy dissipated in exchange of the macroand micro-crack surface. To avoid the formalism...
متن کاملIn-situ ultrasonic monitoring of crack growth under static and dynamic loading conditions [5767-1]
Successful in-situ monitoring of crack initiation and growth is a necessary prerequisite for applying ultrasonic methods to structural health monitoring. For conventional ultrasonic testing methods, a focused beam may be used to directly image the crack tip; however, this method is difficult to apply during fatigue testing because of access limitations and couplant contamination issues. However...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1993
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.59.2844