EPR Properties of Concentrated NdVO4 Single Crystal System
نویسندگان
چکیده
منابع مشابه
EPR Properties of Concentrated NdVO4 Single Crystal System
Single crystals of NdVO4 were grown by the Czochralski method under ambient pressure in a nitrogen atmosphere. Obtained crystals were transparent with strong violet coloring. Temperature and angular dependences of electron paramagnetic resonance (EPR) spectra of the samples in the 3-103 K temperature range were analyzed applying Dyson like lineshape typically used for concentrated magnetic syst...
متن کاملMagneto-Optical properties of GaP single crystal
The temperature dependence of magneto-optical and magneto-photoconductivity measurements were carried out in the range of (200-330) K. A home made optical cryostat was used for the measurements. The measured room temperature value of the energy gap was found to be 2.211 eV. The temperature coefficient of energy gap was found to be -5.48×10-4 eV/K obtained by the optical absorption method and -4...
متن کاملAnalysis of the magnetic properties of nitrogenase FeMo cofactor by single-crystal EPR spectroscopy.
The catalytic center of nitrogenase, the [Mo:7Fe:9S:C]:homocitrate FeMo cofactor, is a S=3/2 system with a rhombic magnetic g tensor. Single-crystal EPR spectroscopy in combination with X-ray diffraction were used to determine the relative orientation of the g tensor with respect to the cluster structure. The protein environment influences the electronic structure of the FeMo cofactor, dictatin...
متن کاملOptical properties of single-crystal Sr2CuO2Cl2.
We report reflectance measurements of single-crystal Sr2CuO2Cl2 over the frequency range between 30 cm and 40 000 cm. Using crystals of 10 mm to 100 mm thickness we were also able to perform transmittance measurements at frequencies below the lowest phonon mode as well as between the highest phonon mode and the charge-transfer gap. The measurements were done on the ~001! surface with ab polariz...
متن کاملOptical properties of single-crystal sapphire fibers.
Single-crystal sapphire fibers have been grown with the laser-heated pedestal-growth method with losses as low as 0.3 dB /m at 2.94 ?m. With the incorporation of a computer-controlled feedback system, fibers have been grown with less than +/-0.5 % diameter variation, or +/-1.5 ?m for a 300- ?m fiber. The losses in these fibers have been reduced further through a postgrowth anneal at 1000 degree...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Magnetic Resonance
سال: 2015
ISSN: 0937-9347,1613-7507
DOI: 10.1007/s00723-015-0659-2