Emulsion templating of poly (acrylic acid) by ammonium hydroxide/sodium hydroxide aqueous mixture for high-dispersed hollow silica nanoparticles
نویسندگان
چکیده
منابع مشابه
Facile Fabrication of Ultrafine Hollow Silica and Magnetic Hollow Silica Nanoparticles by a Dual-Templating Approach
The development of synthetic process for hollow silica materials is an issue of considerable topical interest. While a number of chemical routes are available and are extensively used, the diameter of hollow silica often large than 50 nm. Here, we report on a facial route to synthesis ultrafine hollow silica nanoparticles (the diameter of ca. 24 nm) with high surface area by using cetyltrimethy...
متن کاملEmulsion templating of poly(lactic acid) particles: droplet formation behavior.
Monodisperse poly(DL-lactic acid) (PLA) particles of diameters between 11 and 121 μm were fabricated in flow focusing glass microcapillary devices by evaporation of dichloromethane (DCM) from emulsion droplets at room temperature. The dispersed phase was 5% (w/w) PLA in DCM containing 0.1-2 mM Nile Red and the continuous phase was 5% (w/w) poly(vinyl alcohol) in reverse osmosis water. Particle ...
متن کاملSilica Hollow Spheres by Templating of Catanionic Vesicles
A simple and effective means for obtaining hollow silica particles of controlled diameter from about 60 to 120 nm is presented. The synthesis utilizes equilibrium vesicles as templates for the directed growth of silica. Two different surfactant systems are used to form the vesicular templates: (a) mixtures of cetyltrimethylammonium bromide (CTAB) and sodium perfluorooctanoate (FC7) and (b) mixt...
متن کاملModification of Poly(Ethylene Terephthalate) Fiber by Grafting of Acrylic Acid/Acrylamid for Removel of Pb+2 from Aqueous Solutions
: A new fibrous adsorbent was prepared by grafting Acrylic Acid /Acryl Amide (AA/AAm) co-monomers onto Poly(Ethylene Terephtalat) (PET) fibers. The resulting sorbent has been characterized by Fourier Transform InfraRed spectroscopy (FT-IR), Thermo Gravimetric Analysis (TGA), Scanning Electron Microscopy (SEM) and elemental analysis and studied for the preconcentration and ...
متن کاملAll-acrylic film-forming colloidal polymer/silica nanocomposite particles prepared by aqueous emulsion polymerization.
The efficient synthesis of all-acrylic, film-forming, core-shell colloidal nanocomposite particles via in situ aqueous emulsion copolymerization of methyl methacrylate with n-butyl acrylate in the presence of a glycerol-functionalized ultrafine silica sol using a cationic azo initiator at 60 °C is reported. It is shown that relatively monodisperse nanocomposite particles can be produced with ty...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advanced Powder Technology
سال: 2017
ISSN: 0921-8831
DOI: 10.1016/j.apt.2016.10.010