Efficient laser operation based on transparent Nd:Lu_2O_3 ceramic fabricated by Spark Plasma Sintering

ZrB2-CNTs Nanocomposites Fabricated by Spark Plasma Sintering

ZrB₂-based nanocomposites with and without carbon nanotubes (CNTs) as reinforcement were prepared at 1600 °C by spark plasma sintering. The effects of CNTs on the microstructure and mechanical properties of nano-ZrB₂ matrix composites were studied. The results indicated that adding CNTs can inhibit the abnormal grain growth of ZrB₂ grains and improve the fracture toughness of the composites. Th...

Optically transparent ceramics by spark plasma sintering of oxide nanoparticles

In-situ Fabrication of Transparent Magnesium Aluminate Spinel by Spark Plasma Sintering

Transparent polycrystalline spinel ceramic was fabricated without any sintering aids by spark plasma sintering method of a mixture of Al2O3 and MgO powders for only 10min soak at 1250°C. Densification, microstructure and optical transparency of spinel were examined. The spinel exhibits an in-line transmission of 55% for a visible-wavelength of 470nm and high hardness value of 2040 HV.

Spark plasma sintering of ductile ceramic particles: study of LiF

Densification of cuboidal micrometer-sized lithium fluoride particles as ductile ceramic by spark plasma sintering (SPS) was investigated. Specimens were fabricated at different pressures and temperature conditions, ranging from 2 to 100 MPa at 500 C and from 200 to 700 C under 100 MPa of applied pressure, respectively. Dense specimens of 99 % relative density were fabricated by heating to 500 ...

Effect of SiC nanoparticles addition on mechanical properties and wear resistance of cemented carbides fabricated by spark plasma sintering

WC-10Co cemented carbides containing 1 to 4 wt% SiC nanoparticles were prepared by spark plasma sintering. The effects of SiC content on microstructure, mechanical properties and wear resistance of the sintered materials were studied. Microstructural studies showed that SiC addition resulted in WC grain coarsening. In addition, the hardness decreased with increasing SiC content. However, the fr...