Effects of WC Particle Size and Co Content on the Graded Structure in Functionally Gradient WC-Co Composites
نویسندگان
چکیده
منابع مشابه
Study of milling effect on particle size and mechanical properties of WC-Co composite
The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratios by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350°C at a rate of temperature rise 50°C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly...
متن کاملStudy of milling effect on particle size and mechanical properties of WC-Co composite
The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratios by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350°C at a rate of temperature rise 50°C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly...
متن کاملGeometric and Crystallographic Characterization of WC Surfaces and Grain Boundaries in WC-Co Composites
Electron backscattered diffraction has been used to determine the orientation of WC crystals in a WC-Co composite and atomic force microscopy has been used to measure the shapes of planar sections of the same crystals. A stereological analysis has been used to determine that { } 1010 prism facets and the {0001} basal planes are the WC surfaces that are most frequently in contact with Co. Furthe...
متن کاملThe Hardness and Strength Properties of WC-Co Composites
The industrially-important WC-Co composite materials provide a useful, albeit complicated materials system for understanding the combined influences on hardness and strength properties of the constituent WC particle strengths, the particle sizes, their contiguities, and of Co binder hardness and mean free paths, and in total, the volume fraction of constituents. A connection is made here betwee...
متن کاملEffect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2016
ISSN: 2261-236X
DOI: 10.1051/matecconf/20166706012