Effect of Fatigue Loading Mode on 718 Alloy Fatigue Properties
نویسندگان
چکیده
منابع مشابه
Fatigue and corrosion fatigue properties of Ti-6Al-4V implant grade titanium alloy in Ringer solution
Nowadays modification of metallic biomaterials which are used as implants for bone and hard tissues replacement is considered as an important subject. In the current study, corrosion fatigue properties of Ti-6Al-4V alloy investigated via Rotating-Bending standard test method and then, the results compared with the fatigue properties of the specimens tested in the same conditions. Scanning elect...
متن کاملEffect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy
The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...
متن کاملEffect of creatine loading on neuromuscular fatigue threshold.
The purpose of this investigation was to determine the effect of creatine (Cr) loading on the onset of neuromuscular fatigue by monitoring electromyographic fatigue curves from the vastus lateralis muscle using the physical working capacity at the fatigue threshold (PWC(FT)) test. Using a double-blind random design, 15 women athletes [mean age 19.0 +/- 2.0 (SD) yr] from the university crew team...
متن کاملHigh Frequency Fatigue Test of in 718 Alloy – Microstructure and Fractography Evaluation
J. Belan, Faculty of Mechanical Engineering, University of Žilina, Žilina, Slovak Republic INCONEL alloy 718 is a high-strength; corrosion-resistant nickel chromium material used at -253 °C to 705 °C for production of heat resistant parts of aero jet engine mostly. The fatigue test provided on this kind materials were done via low frequency loading up to this time. Nowadays, needs of results at...
متن کاملLinkage between Ductile Fracture and Extremely Low Cycle Fatigue of Inconel 718 under Multiaxial Loading Conditions
Ductile fracture and extremely low cycle fatigue (ELCF) [1] are two common failure modes in aircraft engines and turbomachinery designs [2]; however, the linkage between these two failure modes under multi-axial loading conditions has never been systematically studied. Inconel 718 (IN718) is one type of high temperature alloys widely used in turbomachines. Specially designed specimens and tests...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Periodica Polytechnica Transportation Engineering
سال: 2018
ISSN: 1587-3811,0303-7800
DOI: 10.3311/pptr.12114