EFFECT OF DUCTILE THERMAL SPRAY COATINGS ON FATIGUE PERFORMANCE OF 7075-T651 ALUMINUM ALLOY
نویسندگان
چکیده
منابع مشابه
Application of the GTN Model in Ductile Fracture Prediction of 7075-T651 Aluminum Alloy
In this paper the capability of Gurson-Tvergaard-Needleman (GTN) model in the prediction of ductile damage in 7075-T651 aluminum alloy is investigated. For this purpose, three types of specimens were tested: Standard tensile bars, Round notched bar (RNB) specimens and compact tension (C(T)) specimens. Standard tensile bar tests were used to obtain the mechanical properties of the material and t...
متن کاملevaluation of fatigue life of friction stir welded 7075-t651 aluminum alloy joints
abstract – aluminium 7075- t651 alloys are widely used in the production of light weight structures requiring a high strength to weight ratio and high corrosion resistance. the effect of processing parameters on fatigue life of 7075- t651 aluminium joints produced by friction stir welding was investigated in the present study. welding samples were made by employing rotating tool speed of 770, 9...
متن کاملSurface Characterizations of Fretting Fatigue Damage in Aluminum Alloy 7075-T6 Clamped Joints: The Beneficial Role of Ni–P Coatings
This paper aims to characterize the surface damage as a consequence of fretting fatigue in aluminum alloy 7075-T6 plates in double-lap bolted joints through XRD, surface profilometry, and SEM analyses. The main focus was on the surface roughness and chemical phase composition of the damaged zone along with the identification of fretting fatigue crack initiations over the surface of the material...
متن کاملEffect of Temperature on Diffusion-Bonded Joint of AZ31 Magnesium and 7075 Aluminum Alloy
In this study, the effect of temperature on the diffusion welding of AZ31 magnesium alloy and 7075 aluminum was discussed. Diffusion welding temperature was the most important parameter since all mechanisms are sensitive to temperature in Diffusion welding method. Intrusive contacts between the two alloys at temperatures of 430, and 440 °C 450 and took 60 min. In all tests constant pressure and...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Canadian Metallurgical Quarterly
سال: 2005
ISSN: 0008-4433,1879-1395
DOI: 10.1179/cmq.2005.44.4.495