Effect of chromate primer on corrosion fatigue in aluminum alloy 7075
نویسندگان
چکیده
منابع مشابه
A Galvanic Corrosion Approach to Investigating Chromate Effects on Aluminum Alloy 2024-T3
The effects of chromate treatment on the corrosion of an aluminum/copper aircraft alloy were examined with a galvanic corrosion apparatus composed of two electrodes and a zero resistance ammeter. Combinations of pure Al, pure Cu, and AA2024-T3 electrodes were immersed in 0.1 M NaCl solution, which was saturated with air, O2 , or argon. Selection of electrode material or differential aeration re...
متن کاملEffect of Temperature on Diffusion-Bonded Joint of AZ31 Magnesium and 7075 Aluminum Alloy
In this study, the effect of temperature on the diffusion welding of AZ31 magnesium alloy and 7075 aluminum was discussed. Diffusion welding temperature was the most important parameter since all mechanisms are sensitive to temperature in Diffusion welding method. Intrusive contacts between the two alloys at temperatures of 430, and 440 °C 450 and took 60 min. In all tests constant pressure and...
متن کاملEffect of Temperature on Diffusion-Bonded Joint of AZ31 Magnesium and 7075 Aluminum Alloy
In this study, the effect of temperature on the diffusion welding of AZ31 magnesium alloy and 7075 aluminum was discussed. Diffusion welding temperature was the most important parameter since all mechanisms are sensitive to temperature in Diffusion welding method. Intrusive contacts between the two alloys at temperatures of 430, and 440 °C 450 and took 60 min. In all tests constant pressure and...
متن کاملCorrosion-Resistant, Chromate-Free Talc Coatings for Aluminum
Aluminum (Al) and Al alloys exhibit unusual passivity when immersed in alkaline lithium (Li) salt solutions. This passivity is a result of precipitation of a continuous, polycrystalline talc coating. Talc coatings persist when removed from the Li salt solution and offer increased corrosion protection during exposure to aggressive environments. Efforts to develop a low-cost, low-toxicity, easily...
متن کاملAccelerated Threshold Fatigue Crack Growth Effect – Powder Metallurgy Aluminum Alloy
Fatigue crack growth (FCG) research conducted in the near threshold regime has identified a room temperature creep crack growth damage mechanism for a fine grain powder metallurgy (PM) aluminum alloy (8009). At very low ∆K, an abrupt acceleration in room temperature FCG rate occurs at high stress ratio (R = Kmin/Kmax). The near threshold accelerated FCG rates are exacerbated by increased levels...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2011
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2011.04.203