Dynamic Compaction of Nd-Fe-B Amorphous Powders.
نویسندگان
چکیده
منابع مشابه
KINETICS OF THE FORMATION OF AMORPHOUS Nd-Fe-B PARTICLES BY CHEMICAL REDUCTION
Fine and ultrafine Nd-Fe-B particles have been obtained from metallic cation reduction by borohydride ions both in water and microemulsions. In this way amorphous particles of different sizes ranging from 4-50 nm to 100-400 nm can be obtained. In this work we will report on the kinetics of the growth of the particles studied by stopped-flow with UV-Vis detection. Quantum effects are suggested f...
متن کاملSintering of Nd-Fe-B Magnets from Dy Coated Powder
High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundar...
متن کاملRadiation-Induced Demagnetization of Nd-Fe-B Permanent Magnets
Introduction The Advanced Photon Source (APS), as well as other third-generation synchrotron light sources, uses permanent magnets in the insertion devices to produce x-rays for scientific research [1,2]. When placed in a high-energy storage ring, these permanent magnets are subjected to irradiation from synchrotron radiation, high-energy bremsstrahlung, and bremsstrahlung-produced neutrons. Pr...
متن کاملImpulse Magnetization of Nd-Fe-B Sintered Magnets for Sensors
Magnetization of large Nd-Fe-B sintered permanent magnets is still challenging. This type of permanent magnet is electrically conductive, so impulse magnetization causes a flow of eddy currents which prevent magnetization of the whole volume of the magnet. The paper deals with the impulse magnetization of sintered Nd-Fe-B permanent magnets and shows a method for the determination of suitable pa...
متن کاملCOERCIVITY AND THERMAL REMAGNETIZATION OF SINTERED Nd-Fe-B
Statistical methods are used to estimate coercivity J Hc and thermal remagnetization of uniaxially nucleationcontrolled permanent magnetic materials. Sintered Nd-Fe-B consists of the tetragonal magnetic Nd2FelrB phase with a volume fraction w = 80 % and of nonmagnetic phases. At temperatures above T, rz 150 K the tetragonal axis is the easy direction of magnetization [I]. It is well known [2] t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1995
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.42.304