DRY SLIDING WEAR BEHAVIOR OF HYBRID METAL MATRIX COMPOSITES
نویسندگان
چکیده
منابع مشابه
THE EFFECT OF VARIOUS PARAMETERS ON DRY SLIDING WEAR BEHAVIOR AND SUBSURFACE OF AGED HYBRID METAL MATRIX COMPOSITES USING TAGUCHI TECHNIQUE
The effects of applied load, sliding speed and sliding distance on the dry sliding wear behavior of aged Al-SiCp-Gr composites were investigated. The specimen were fabricated by stir-casting technique. The pin-on-disc wear testing machine was used to investigate the wear rate by design of experiments based on L27 using Taguchi technique. Sliding distance was the most important variable that inf...
متن کاملDry Sliding Wear Behavior of Epoxy-Rubber Dust Composites
Composite pins of rubber dust collected from tyre retreading centres of trucks, cars and buses etc.and epoxy with weight percentages of 10. 15, and 20 % of rubber (weight fractions of 9, 13 and 17 % respectively) have been prepared in house with the help of a split wooden mould. The pins were tested in a pin-on-disc wear monitor to determine the co-efficient of friction and weight losses with v...
متن کاملDRY SLIDING WEAR BEHAVIOUR OF STIR CAST LM 25/ZrO2 METAL MATRIX COMPOSITES
In the present study, an investigation into wear properties has been carried out to identify the influence of ZrO2 as the reinforcement material on the LM25 MMC composite. Aluminum LM25 is selected as the base material, and it is reinforced with varying proportions of 0, 3, 6, 9, 12 and 15% of zirconia (ZrO2) manufactured by stir casting. Six tensile test and wear test samples were prepared acc...
متن کاملDry Sliding Wear and Mechanical Behavior of Aluminium / Fly ash / Graphite Hybrid Metal Matrix Composite Using Taguchi Method
The experimental investigation of hybrid metal matrix composites with fly ash and graphite reinforced aluminium alloy (Al 6061) composites samples, processed by stir casting route are reported. The aluminium alloy was reinforced with 3 wt.%, 6 wt.%, 9 wt.% fly ash and fixed 3 wt.% of graphite to mixture the hybrid composite. Hardness of the hybrid composite were tested it was found that when th...
متن کاملMicrostructure and Dry-Sliding Wear Behavior of B4C Ceramic Particulate Reinforced Al 5083 Matrix Composite
B4C ceramic particulate–reinforced Al 5083 matrix composite with various B4C content was fabricated successfully via hot-press sintering under Argon atmosphere. B4C particles presented relative high wettability, bonding strength and symmetrical distribution in the Al 5083 matrix. The hardness value, friction coefficient and wear resistance of the composite were higher than those of the Al 5083 ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Research in Engineering and Technology
سال: 2014
ISSN: 2321-7308,2319-1163
DOI: 10.15623/ijret.2014.0315104