Development of probabilistic primary water stress corrosion cracking initiation model for alloy 182 welds considering thermal aging and cold work effects
نویسندگان
چکیده
We experimentally investigated the effects of thermal aging and cold work on microstructure, mechanical properties, primary water stress corrosion cracking (PWSCC) initiation time for Alloy 182 welds. The PWSCC were modeled based plastic energy concept data this study previous reports by considering censored data. Based results, it is estimated that resistance weld firstly increases then decreases with when applied kept constant.
منابع مشابه
Corrosion-Induced Concrete Cracking Model Considering Corrosion-Filled Paste
A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can q...
متن کاملA Probabilistic-mechanistic Approach to Modeling Stress Corrosion Cracking Propagation in Alloy 600 Components with Applications
Title of Document: A PROBABILISTIC-MECHANISTIC APPROACH TO MODELING STRESS CORROSION CRACKING PROPAGATION IN ALLOY 600 COMPONENTS WITH APPLICATIONS
متن کاملEffect of Hydrogen on Corrosion and Stress Corrosion Cracking of AZ91 Alloy in Aqueous Solutions
The effect of hydrogen on the corrosion and stress corrosion cracking of the magnesium AZ91 alloy has been investigated in aqueous solutions. Hydrogen produced by corrosion in water diffuses into, and reacts with the Mg matrix to form hydride. Some of the hydrogen accumulates at hydride/Mg matrix (or secondary phase) interfaces as a consequence of slow hydride formation and the incompatibility ...
متن کاملAn Outrun Competition of Corrosion Fatigue and Stress Corrosion Cracking on Crack Initiation in a Compressor Blade
First row rotating blades of four axial-flow compressors were prematurely fractured. Previous investigations showed that the site atmosphere contains corrosive compounds which lead to an increase in possibility of pitting on the blades. It was also revealed that the crack was originated from two corrosion pits. Thus, this work is conducted to ascertain which of fatigue or stress corrosion crack...
متن کاملAn Investigation on Corrosion and Stress Corrosion Cracking initiation of a Ferritic Stainless Steel in a Tertiary Amine Solution
The present study focused on stress corrosion cracking (SCC) and corrosion behavior of ferritic stainless steel (grade 430) in activated methyl diethanolamine (aMDEA) solution, which is classified as a tertiary amine. In this regard, cyclic polarization and U-bend tests were performed in CO2 loaded aMDEA with different concentrations at 25 and 70 °C to observe corrosion behavior and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nuclear Engineering and Technology
سال: 2021
ISSN: ['1738-5733', '2234-358X']
DOI: https://doi.org/10.1016/j.net.2020.12.005