Development of galvanized high-strength high-carbon steel wire.
نویسندگان
چکیده
منابع مشابه
Real-time monitoring of laser welding of galvanized high strength steel in lap joint configuration
Two different cases regarding the zinc coating at the lap joint faying surface are selected for studying the influence of zinc vapor on the keyhole dynamics of the weld pool and the final welding quality. One case has the zinc coating fully removed at the faying surface; while the other case retains the zinc coating on the faying surface. It is found that removal of the zinc coating at the fayi...
متن کاملInfluence of the Manufacturing Process on Defects in the Galvanized Coating of High Carbon Steel Wires
This study is a detailed failure analysis of galvanized high carbon steel wires, which developed coating cracks during the torsion test performed as a quality control at the end of the manufacturing process. Careful visual inspections showed that the cracks are already present in the coating before the torsion test. In order to explain the origin of these cracks, systematic metallographic inves...
متن کاملDeveloping Very Fine Nanopearlitic Structure in a High Carbon Steel Wire before Drawing
The effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. In this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. The results were the minimum interlamellar spacing of 35 nm and maximum ulti...
متن کاملStudies on defects in galvanized coating on steel wire
Causes for deposition of defective galvanized coating (lumpy deposition of coating during hot dip galvanizing) of carbon-steel wire have been investigated. It is established that the lumpy deposition is caused due to segregation of silicon on the surface of steel wire. Due to this change in composition of the steel at surface, the regions get modified and lie in Sandelin hyper reactive zone. Th...
متن کاملBond of High Strength Concrete with High Strength Reinforcing Steel
This paper presents a study about the bond of high strength concrete with high strength steel. Fourteen pull out tests were carried out to determine the bond. The concrete strength was about 70 MPa and the steel was a 500 MPa grade. Bar diameters used were 12, 16, 20, 25, 28, 32 and 36 mm. In order to investigate the effect of cover, each test was done twice, once in a 240 mm diameter concrete ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Iron and Steel Institute of Japan
سال: 1986
ISSN: 0021-1583,1881-1183
DOI: 10.2355/isijinternational1966.26.1059