Deposition and characterization of Ca3Ce(PO4)3 phase in coating to protect stainless steel 316L
نویسندگان
چکیده
RF sputtering was achieved to get Ca3Ce(PO4)3 phase from target of 60wt%CeO2/TCP on stainless steel 316L surface for bioapplication. The selection ceria and tricalcium phosphate is according fact the importance these materials in biomedical media. produced confirmed by XRD analysis (JCPDS card No. 09-0169) with important 2θ values at (≈ 28.4, 33.7, 46.6 44.7). FESEM/EDS exam showed smoother indication appear this through compact layer deposited particles. EDS mapping presence main elements substrate addition Ce, Ca, P, O. AFM images shows uniform distribution particles indicates lower average roughness diameter coated specimen compared substrate.
منابع مشابه
Characterization of CrN/TiN PVD Coatings on 316L Stainless Steel
In order to further enhance tribological properties 316 Low carbon stainless steel (L SS) used on mechanical parts. CrN/TiN with DC magnetron sputtering sources was carried out on PVD 316 L SS. The micro structure of the CrN/TiN coatings were investigated by Scanning electron microscope (SEM), X-ray Diffraction (XRD) and tribology properties were investigated on a Pin on Disc friction and wear ...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملCharacterization of SiO2-TiO2 Coatings on 316l Stainless Steel Substrates
This paper reports nano-structured SiO2-TiO2 coatings using the sol-gel technique on 316L steel substrates. Nanoindentation, surface analysis and corrosion resistance tests were performed on different samples. The nanomechanical tests allowed to compare uncoated steel samples (Eavg = 193.24 GPa and mean hardness of 2.63 GPa and coated steel samples (Eavg = 287.38 GPa and mean hardness of 5.74 G...
متن کاملalumina nanostructured coating for corrosion protection of 316l stainless steel
nanostructured alumina thin films were coated on stainless steel by sol-gel dip coating method. in order to prevent crack formation, al2o3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. effects of calcination temperature and withdrawal speed on structural properties were analyzed using xrd and sem. topography and thickness of coatings were analyzed by ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nucleation and Atmospheric Aerosols
سال: 2021
ISSN: ['0094-243X', '1551-7616', '1935-0465']
DOI: https://doi.org/10.1063/5.0067094