Delamination analysis of metal–ceramic multilayer coatings subject to nanoindentation
نویسندگان
چکیده
منابع مشابه
Delamination of multilayer thermal barrier coatings
Multilayer thermal barrier coatings (TBCs) on superalloy substrates are comprised of an intermetallic bond coat, a thermally grown oxide (TGO) layer, and a porous zirconia top coat that provides thermal protection. The TGO attains a thickness of 1±10 lm prior to failure, while the bond coat and zirconia layer are each about 50±100 lm thick. The preferred method for manufacturing TBCs comprises ...
متن کاملPlastic Deformation Induced by Nanoindentation Test Applied on ZrN/Si3N4 Multilayer Coatings
ZrN/Si3N4 multilayer coating that alternates with either nanocrystalline ZrN or amorphous Si3N4 interlayers was fabricated by reactively magnetron sputtering in an Ar-N2 mixture atmosphere. The thicknesses of the nanocrystalline ZrN and the amorphous Si3N4 interlayers are ~12.5 and 2.5 nm, respectively. The ZrN/Si3N4 coating exhibits a promoted hardness of 28.6 ± 1.2 GPa when compared to the bi...
متن کاملMULTI FRACTURE/DELAMINATION ANALYSIS OF COMPOSITES SUBJECTED TO IMPACT LOADINGS
A combined finite/ discrete element method is presented for modelling of composite specimens subjected to dynamic/impact loadings. The main task is set on developing an algorithm for simulation of potential bonding and debonding/delamination phenomena during impact or general dynamic loading conditions. In addition, full fracture analysis can also be performed. The proposed approach adopts a ge...
متن کاملIn-situ Stress Analysis of Multilayer Environmental Barrier Coatings
The biaxial stress and thermal expansion of multilayer doped-aluminosilicate environmental barrier coatings were measured in-situ during cooling using microfocused high-energy X-rays in transmission. Coating stresses during cooling from 1000oC were measured for as-sprayed and thermally cycled samples. In the as-sprayed state, tensile stresses as high as 75 MPa were measured in the doped-alumino...
متن کاملLaser-resistance sensitivity to substrate pit size of multilayer coatings
Nanosecond laser-resistance to dielectric multilayer coatings on substrate pits was examined with respect to the electric-field (E-field) enhancement and mechanical properties. The laser-induced damage sensitivity to the shape of the substrate pits has not been directly investigated through experiments, thus preventing clear understanding of the damage mechanism of substrate pits. We performed ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Surface and Coatings Technology
سال: 2016
ISSN: 0257-8972
DOI: 10.1016/j.surfcoat.2016.01.038