Deformation Mechanisms in Nanocrystalline Materials
نویسندگان
چکیده
منابع مشابه
Deformation twinning in nanocrystalline materials
Nanocrystalline (nc) materials can be defined as solids with grain sizes in the range of 1–100 nm. Contrary to coarse-grained metals, which become more difficult to twin with decreasing grain size, nanocrystalline face-centered-cubic (fcc) metals become easier to twin with decreasing grain size, reaching a maximum twinning probability, and then become more difficult to twin when the grain size ...
متن کاملContinuum Models of Deformation Mechanisms in Nanocrystalline Metals
Nanocrystalline metals are polycrystalline metals with grain sizes in the nanometer range. They have attracted significant interest in recent years due to their unique mechanical and electrical properties. The main objective of this thesis is to develop continuum-scale descriptions of nanoscale deformation and failure mechanisms in nanocrystalline metals. The research has focused on three speci...
متن کاملDeformation twinning in nanocrystalline aluminum.
We report transmission electron microscope observations that provide evidence of deformation twinning in plastically deformed nanocrystalline aluminum. The presence of these twins is directly related to the nanocrystalline structure, because they are not observed in coarse-grained pure aluminum. We propose a dislocation-based model to explain the preference for deformation twins and stacking fa...
متن کاملStresses in nanocrystalline materials
Thin film Ni-Cu diffusion couples (individual layer thicknesses: 50 nm) were prepared by direct-current magnetron sputtering on silicon substrates. Interdiffusion and solid-solution formation, the associated changes of microstructure and the evolution of mechanical stresses of the Ni-Cu diffusion couples during thermal treatments were investigated employing ex-situ X-ray diffraction phase and t...
متن کاملDeformation of electrodeposited nanocrystalline nickel
The mechanisms of deformation and damage evolution in electrodeposited, fully dense, nanocrystalline Ni with an average grain size of ~30 nm and a narrow grain size distribution were investigated by recourse to (i) tensile tests performed in situ in the transmission electron microscope and (ii) microscopic observations made at high resolution following ex situ deformation induced by compression...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallurgical and Materials Transactions A
سال: 2009
ISSN: 1073-5623,1543-1940
DOI: 10.1007/s11661-009-0103-z