Formation of bulk metallic glass in quaternary Ti-Zr-Cu-Ni alloys by relatively slow cooling from the melt is reported. Thick strips of metallic glass were obtained by the method of metal mold casting. The glass forming ability of the quaternary alloys exceeds that of binary or ternary alloys containing the same elements due to the complexity of the system. The best glass forming alloys such as...
متن کاملZr–Cu–Ni–Al bulk metallic glasses with superhigh glass-forming ability
Zr–Cu–Ni–Al quaternary amorphous alloy compositions with varying glass-forming ability are developed by an efficient method of proportional mixing of binary eutectics. The critical diameter of the glassy sample is improved from 6 mm for Zr53Cu18.7Ni12Al16.3 to 14 mm for Zr50.7Cu28Ni9Al12.3 by straightforwardly adjusting the eutectic unit’s coefficients. The drastic improvement in GFA is attribu...
متن کاملGlass Forming Ability and Corrosion Resistance of Zr-Cu-Ni-Al-Ag Bulk Metallic Glass
Zr70−xCu12.5Ni10Al7.5Agx (x = 0–10) bulk metallic glasses (BMGs) have been prepared by copper mold casting. The glass-forming ability (GFA) and corrosion behavior of Zr-based BMGs have been investigated. It is found that the GFA of Zr-based BMGs first increases and then decreases with the increase of the Ag content, and the best glass former is Zr65Cu12.5Ni10Al7.5Ag5 with the maximum thickness ...
متن کاملStructural origins for the high plasticity of a Zr–Cu–Ni–Al bulk metallic glass
The structural origins for the high plasticity of a Zr53Cu18.7Ni12Al16.3 (at.%) bulk metallic glass are explored. Under plastic flow conditions, in situ synchrotron high-energy X-ray diffraction reveals that the atomic strain saturates to the closest packing in the longitudinal direction of the applied load while atoms yield in the transverse plane. Scanning electron microscopy investigation re...
متن کاملSupercooled melting in multicomponent Zr–Al–Cu–Ni diffusion couples
Diffusion couples combining a hcp Zr90Al10 supersaturated solid solution with a fcc Cu64Ni36 solid solution were annealed at 410 °C for different times. The reaction at the interface was investigated by transmission electron microscopy and energy dispersive x-ray spectroscopy. The investigations show the formation of a noncrystalline layer at the interface between the two solid solutions that g...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2007
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.mf200615