Decay resistance, hardness, water absorption, and thickness swelling of a bagasse fiber/plastic composite
نویسندگان
چکیده
منابع مشابه
investigation on the decay resistance of bagasse-polypropylene composite
in this research, the decay resistance of bagasse-polypropylene composite has been evaluated. the scope of research was to assess the effect of different weight percentages of bagasse (40, 55 and 70%) and coupling agent, (mapp) maleic anhydride grafted polypropylene (0, 4 and 6%) on the fungal decay of the composite. astm d1413-99 modified test method was used to carry out the decay test, trame...
متن کاملFlexural Properties and Orthotropic Swelling Behavior of Bagasse/thermoplastic Composites
The flexural properties of commercial bagasse-filled polyethylene (PE) and polypropylene (PP) composites were determined as a function of strain rate at room temperature. The applied strain rates were 1.5 ×10, 3.75×10, 7.5×10, and 1.5×10 s. The flexural modulus tended to increase linearly for the two types of composites with the logarithm of strain rate. The bending strength of polypropylene co...
متن کاملInvestigation of Swelling Behavior and Mechanical Properties of a pH-Sensitive Superporous Hydrogel Composite
The objective of the present study is to develop and investigate the swelling behavior of pH-sensitive Superporous Hydrogel (SPH) and SPH composite (SPHC). A novel superporous hydrogel containing poly (methacrylic acid-co-acrylamide) was synthesized from methacrylic acid and acrylamide through the aqueous solution polymerization, using N,N-methylenebisacrylamide as a crosslinker and ammonium...
متن کاملeffect of postharvest application of chitosan and calcium chloride on decay and quality attributes of sweet cherry
چکیده ندارد.
15 صفحه اولDEVELOPMENT OF HARDNESS IN A Fe- BASED NANO-COMPOSITE ALLOY
Achieving extreme hardness in the newly synthetic steel formed by converting from initial amorphous state to subse-quent crystalline structure –named as devitrification process- was studied in this research work. Results of TEM observa-tions and XRD tests showed that crystallized microstructure were made up four different nano-scale phases i.e., α-Fe, Fe 36 Cr12 Mo10 , Fe 3 C and Fe3 B. More, V...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: BioResources
سال: 2011
ISSN: 1930-2126,1930-2126
DOI: 10.15376/biores.6.3.3289-3299