Crystal structure of samarium nickel aluminide, Sm4Ni6Al23
نویسندگان
چکیده
منابع مشابه
Vacancy Mobility in Nickel Aluminide versus Composition
The fractional concentration of Ni-vacancies in NiAl at high temperature has been determined for compositions between 50 and 53 at.% Ni from measurements using perturbed angular correlation of gamma rays (PAC). The vacancies were detected by quadrupole interactions induced at nearby In/Cd impurity probes present on the Al sublattice in high dilution. One set of measurements was made at high tem...
متن کاملEquilibrium Defects and Concentrations in Nickel Aluminide
Perturbed angular correlation of gamma rays was applied to determine properties of equilibrium defects in B2 NiAl near the stoichiometric composition. Point defects were detected through quadrupole interactions they induce at In probe atoms on the Al sublattice. Well-resolved signals were observed for probe atoms having zero, one or two Ni-vacancies (VNi) in the first neighbor shell. The fracti...
متن کاملThe Effects of Beryllium Additions on the Oxidation of Nickel Aluminide and Titanium Aluminide Based Intermetallics
The effects of Be additions on the oxidation behavior of ~-NiAl in moist air at 1000°C and borderline alumina-forming y (TiAI) + Laves Ti-Al-Cr based alloys at 800°C and 1000°C in dry and moist air were investigated. The addition of Be to ~-NiAl suppressed the formation of transient alumina, and resulted in the formation of a protective BeAl20 4 spinel phase. In dry air, the addition of Be to t...
متن کاملCyclic oxidation-induced cracking of platinum-modified nickel-aluminide coatings
Short cracks, extending to the interdiffusion zone, have been observed in platinum-modified nickel-aluminide diffusion coatings on single-crystal CMSX-4 superalloys after these have been subject to short (10 min) rapid thermal cycles. The cracks were revealed after removing the thermally grown oxide formed during cycling on the coating surfaces. Cracking was observed for coatings subject to the...
متن کاملSynthesis of nickel–aluminide foams by pack-aluminization of nickel foams
Nickel–aluminide foams were synthesized from unalloyed nickel foams by using a two-step, high-activity pack-aluminizing process at 1273 K. After processing, the nickel–aluminide foams exhibited the original structure of the original nickel foams (open-cells with hollows struts and low density). Single-phase NiAl foams, with average composition within 1 wt.% of stoichiometry and with 92% open po...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Zeitschrift für Kristallographie - New Crystal Structures
سال: 2004
ISSN: 2197-4578,1433-7266
DOI: 10.1524/ncrs.2004.219.14.87