Crack Growth Resistance of 18 Ni Maraging Steel in Rotary Bending Fatigue
نویسندگان
چکیده
منابع مشابه
Bending Fatigue Failures in Valve Steel
In the present paper the effect of defects (viz. pits, gouges and oxide inclusions) will be reported. Although certain defects were uniformly distributed over the specimen surface, the majority of all fractures started in the edge region. An explanation to this behaviour is presented in terms of stress enhancement in the edge regions due to edge deflections.
متن کاملRotary-bending fatigue characteristics of medical-grade Nitinol wire.
The rotary bending fatigue properties of medical-grade Nitinol wires were investigated under conditions of 0.5-10% strain amplitudes to a maximum of 10(7) cycles. The results from this study provide insight into the behavior of Nitinol under fully reversed (εmin/εmax=-1) fatigue conditions for three compositions, two surface conditions and three test temperatures. For pseudoelastic conditions t...
متن کاملAnalysis of Fatigue Crack Paths in Cold Drawn Pearlitic Steel
In this paper, a fracto-metallographic analysis was performed on the cracked specimens of cold drawn pearlitic steel subjected to fatigue tests. Fatigue cracks are transcollonial and exhibit a preference for fracturing pearlitic lamellae, with non-uniform crack opening displacement values, micro-discontinuities, branchings, bifurcations and frequent local deflections that create microstructural...
متن کاملFatigue Crack Detection and Sizing in Welded Steel Structures
The paper gives an outline of the non-destructive evaluation (NDE) methods currently being pursued at the Admiralty Marine Technology Establishment, Dunfermline, Scotland. The methods are being used to locate and characterise fatigue cracks in high yield strength welded steel structures. The techniques have been applied principally to large fatigue models (5' and 9' diameter) as part of a compr...
متن کاملEffect of aging and deformation on the microstructure and properties of Fe-Ni-Ti maraging steel
The age-hardening behavior of Fe−25.3Ni−1.7 Ti (wt pct) alloy both in undeformed specimens and in specimens cold deformed by 10 or 20 pct prior to aging was studied. The microstructural changes during aging were observed using transmission electron microscopy (TEM) and atom probe analysis and there were related to the mechanical properties as measured by microhardness and shear punch testing. A...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1983
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.49.699