Corrosion Fatigue Fracture Behavior of WC Cermet Sprayed Mild Steel
نویسندگان
چکیده
منابع مشابه
FRACTURE AND FATIGUE BEHAVIOR OF WC-Co AND WC-CoNi CEMENTED CARBIDES
The fracture and fatigue characteristics of several cemented carbide grades are investigated as a function of their microstructure. In doing so, the influence of binder chemical nature and content (Co and 76wt%Co-24wt%Ni), as well as carbide grain size on hardness, flexural strength, fracture toughness and fatigue crack growth (FCG) behavior is evaluated. Mechanical testing is combined with a d...
متن کاملFracture Mechanics and Corrosion Fatigue
The development and current state-of-the-art in fracture mechanics in relation to studies of environment-enhanced fatigue-crack growth (corrosion fatigue) and fatigue-crack growth per se are reviewed. Patterns of response of materials to different loading and environmental conditions are considered in terms of the probable mechanisms for environmental embrittlement. The usefulness of the fractu...
متن کاملCorrosion Behavior of Polypyrrole/Mesoporous Silica Nanocontainers Coatings on the Mild Steel
The idea of smart corrosion inhibition is basis on either inhibitor consumption where it is needed or reducing harmful matrix interaction with it. In addition, applying corrosion inhibitor in a coating causes many problems such as loss of inhibition capability, coating degradation, or both. A useful technique to overcome th...
متن کاملCorrosion Behavior of Stainless Steel Clad Rebar
Stainless steel clad rebar (SCR) was investigated because it may become a cost-effective means of controlling corrosion in concrete under very aggressive environments. Sound SCR (316L cladding) resisted corrosion in saturated Ca(OH)2 solution (SCS) with up to 5 wt% chloride. Cladding breaks on SCR induced significant corrosion of exposed underlying CS in SCS with only 1 wt% chloride. A computer...
متن کاملHigh-Cycle Microscopic Corrosion Fatigue Behavior and Life Prediction of 25CrMo Steel Used in Railway Axle
The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate dur...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2004
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.53.1228