Corrosion and Nanomechanical Behaviors of 16.3Cr-0.22N-0.43C-1.73Mo Martensitic Stainless Steel
نویسندگان
چکیده
منابع مشابه
Electrochemical Characterization of a Martensitic Stainless Steel
This paper focused on the characterization of electrochemical behavior of a martensitic stainless steel in the acidic solutions. For this purpose, electrochemical parameters were derived from potentiodynamic polarization, Mott Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that corrosion current density of AISI 420 ...
متن کاملMicrostructure, Mechanical and Corrosion Properties of Friction Stir Welding High Nitrogen Martensitic Stainless Steel 30Cr15Mo1N
High nitrogen martensitic stainless steel 30Cr15Mo1N plates were successfully welded by friction stir welding (FSW) at a tool rotation speed of 300 rpm with a welding speed of 100 mm/min, using W-Re tool. The sound joint with no significant nitrogen loss was successfully produced. Microstructure, mechanical and corrosion properties of an FSW joint were investigated. The results suggest that the...
متن کاملElectrochemical Characterization of a Martensitic Stainless Steel
This paper focused on the characterization of electrochemical behavior of a martensitic stainless steel in the acidic solutions. For this purpose, electrochemical parameters were derived from potentiodynamic polarization, Mott Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that corrosion current density of AISI 420 ...
متن کاملCorrosion Behavior of Stainless Steel Clad Rebar
Stainless steel clad rebar (SCR) was investigated because it may become a cost-effective means of controlling corrosion in concrete under very aggressive environments. Sound SCR (316L cladding) resisted corrosion in saturated Ca(OH)2 solution (SCS) with up to 5 wt% chloride. Cladding breaks on SCR induced significant corrosion of exposed underlying CS in SCS with only 1 wt% chloride. A computer...
متن کاملCorrosion at Sulphide Inclusions in Stainless Steel
Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly corroded, which might be due to CU2S deposition on the surface of corroding inclusions. In contr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Science and Technology
سال: 2016
ISSN: 1598-6462
DOI: 10.14773/cst.2016.15.6.281