Corrodibility and Adherence of Reinforced Concrete Rebars Electroplated with Zinc and Zinc-Nickel Alloys
نویسندگان
چکیده
منابع مشابه
CORROSION BEHAVIOR OF ZINC COATED STEEL REBAR IN HIGH-STRENGTH REINFORCED CONCRETE
A large number of reinforced concrete structures subjected to chloride ions. Two basicapproaches for preventing corrosion of reinforcing steel embedded in concrete are: Increasing theconsolidation of concrete and using different coating on rebars. In present research steel rebarsare coated in different ways: a) 40 µm of zinc electroplated on steel rebar b) Zinc powder withepoxy paste (zinc rich...
متن کاملZinc-Nickel Binary Alloys Electrodeposition of Steel Using Pulse Current
Zinc-Nickel electrodeposits have been widely adopted for surface treatment of automobile steel sheet for high corrosion resistance. In this work the effect of pulse parameters on the Zn-Ni alloy electrodeposits was investigated. The hardness, thickness, corrosion resistance and composition of deposits thus produced were investigated. The surface topography of the deposits was also observed in S...
متن کاملZinc-Nickel Binary Alloys Electrodeposition of Steel Using Pulse Current
Zinc-Nickel electrodeposits have been widely adopted for surface treatment of automobile steel sheet for high corrosion resistance. In this work the effect of pulse parameters on the Zn-Ni alloy electrodeposits was investigated. The hardness, thickness, corrosion resistance and composition of deposits thus produced were investigated. The surface topography of the deposits was also observed in S...
متن کاملHydrogen Embrittlement of High Strength Steel Electroplated with Zinc-cobalt Alloys
Slow strain rate tests were performed on quenched and tempered AISI 4340 steel to measure the extent of hydrogen embrittlement caused by electroplating with zinc-cobalt alloys. The effects of bath composition and pH were studied and compared with results for electrodeposited cadmium and zinc-10%nickel. It was found that Zinc-1%cobalt alloy coatings caused serious hydrogen embrittlement (EI 0.63...
متن کاملzinc-nickel binary alloys electrodeposition of steel using pulse current
zinc-nickel electrodeposits have been widely adopted for surface treatment of automobile steel sheet for high corrosion resistance. in this work the effect of pulse parameters on the zn-ni alloy electrodeposits was investigated. the hardness, thickness, corrosion resistance and composition of deposits thus produced were investigated. the surface topography of the deposits was also observed in s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research
سال: 2019
ISSN: 1980-5373,1516-1439
DOI: 10.1590/1980-5373-mr-2018-0915