Continuous production of magnetic iron oxide nanocrystals by oxidative precipitation
نویسندگان
چکیده
منابع مشابه
Iron Oxide Nanocrystals for Magnetic Hyperthermia Applications
Magnetic nanocrystals have been investigated extensively in the past several years for several potential applications, such as information technology, MRI contrast agents, and for drug conjugation and delivery. A specific property of interest in biomedicine is magnetic hyperthermia-an increase in temperature resulting from the thermal energy released by magnetic nanocrystals in an external alte...
متن کاملMagnetic iron oxide nanoparticles, Polyethylene glycol, Surfactant, Superparamagnetic, Chemical co-precipitation
In this study, magnetic iron oxide nanoparticles (Fe3O4) with the size range of 20-30 nm were prepared by the modified controlled chemical co-precipitation method from the solution of ferrous/ferric mixed salt-solution in alkaline medium. In this process polyethylene glycol was used as a surfactant to prevent the solution from agglomeration. The prepared magnetic nanoparticles were characterize...
متن کاملStructure and Magnetic Properties of Oxide Nanoparticles of Fe-Co-Ni Synthesized by Co-Precipitation Method
Oxide nanoparticles of Fe-Co-Ni were prepared in six different compositions by co-precipitation method. The as-synthesized nanoparticles were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron microscope (FESEM), Fourier Transform Infrared (FT-IR) and Vibrating Sample Magnetometer (VSM). It was found that the nanoparticles had mean crystalline size of 30-55 nm and spher...
متن کاملSynthesis of monodisperse iron oxide nanocrystals by thermal decomposition of iron carboxylate salts.
Iron oxide (Fe(3)O(4), magnetite) nanocrystals of 6 to 30 nm with narrow size distributions (sigma = 5-10%) were prepared by the pyrolysis of iron carboxylate salts.
متن کامل2D to 3D crossover of the magnetic properties in ordered arrays of iron oxide nanocrystals.
The magnetic 2D to 3D crossover behavior of well-ordered arrays of monodomain γ-Fe(2)O(3) spherical nanoparticles with different thicknesses has been investigated by magnetometry and Monte Carlo (MC) simulations. Using the structural information of the arrays obtained from grazing incidence small-angle X-ray scattering and scanning electron microscopy together with the experimentally determined...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chemical Engineering Journal
سال: 2020
ISSN: 1385-8947
DOI: 10.1016/j.cej.2020.124593