Abstract: A combination of a finite element method (FEM) algorithm with ANSYS codes and post image processing of NDT ultrasonic images along with laboratory cooling experiments and microstructural analysis provide a guideline to determine the optimum cooling rate for any grade of steel in which the highest productivity can be achieved without any degradation of the cast steel products. The sugg...
متن کاملPorosity Control and Fatigue Behavior in A356-T61 Aluminum Alloy
Much work has been done, in recent years, to characterize the factors that cause porosity in aluminum castings, and to analyze the impact of porosity or microstructural parameters on fatigue life. What has yet to be done is systematically separate out the effects of dendrite arm spacing and largest pore size from each other, and from the underlying chemical and process parameters that influence...
متن کاملEFFECTS OF HOT ISOSTATIC PRESSING ON THE TENSILE PROPERTIES OF A356 CAST ALLOY
The influences of age hardening and HIP (Hot Isostatic Pressing) on the mechanical properties of A356 (Al 7Si 0.6 Mg) casting alloys were studied. Cast bars were homogenized, heated and maintained at a temperature of 540°C for a duration of 2 hours, followed by rapid cooling in a polymeric solution. The castings were age hardened at 180°C for a duration of 4 hours before being subjected to HIP ...
متن کاملThe Effects of Mould Materials on Microstructure and Mechanical Properties of Cast A356 Alloy
Abstract In this study, the effects of mould materials on microstructure and mechanical properties of cast A356 Al alloy were investigated. The alloy was poured into three different moulds. Then the samples were homogenised and applied T6 heat treatment. The optical, Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) studies were made. Secondary dendrite arm spacing (SD...
متن کاملCompressive creep behavior of cast Bi2Te3
In thermoelectric devices, Bi2Te3 must be able to operate under high temperature gradients for very long times (years) without appreciable deformation, while being subjected to stresses created by internal thermal mismatch and external forces (e.g., vibrations). The deformation rate of cast, coarsegrained Bi2Te3 was measured under uniaxial compressive stresses from 2 to 16 MPa at temperatures b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Science and Engineering: A
سال: 2012
ISSN: 0921-5093
DOI: 10.1016/j.msea.2012.03.106