Combined Corrosion and Wear of Aluminium Alloy 7075-T6
نویسندگان
چکیده
منابع مشابه
Wear behaviour of AA6061 aluminium alloy and its composites
This study investigates the wear resistance of four AA6061 MMCs together with the monolithic AA6061 alloy, all in the T6 condition, using a pin-on-disc test. In addition to the widely studied 20 vol.% Saffil MMCs, the present investigation considered a hybrid of 11% Saffil + 20% Sic, and a high volume fraction Sic, MMC. AA6061 + 60% Sic,. The wear behaviour against P400 Sic grit adhesive bonded...
متن کاملTENSILE AND FRACTURE CHARACTERISTICS OF A SIC- PARTICLE-REINFORCED 7075 ALUMINIUM ALLOY
Fracture behavior of a 7075 aluminium alloy reinforced with 15 Vol%. SiC particles was studied after T6 and annealing heat treatments under uniaxial tensile loading at room temperature. The scanning electron microscopy of fractured surfaces and EDS analysis showed:, that fracture mechanism changed from due mainly to fractured particle in T6 condition to interface decohesion in samples in anneal...
متن کاملStudies of Corrosion of Aluminium and 6063 Aluminium Alloy in Phosphoric Acid Medium
The corrosion behaviour of aluminium and6063 aluminium alloy was investigated in phosphoric acid of different concentrations at different temperatures. The study was done by electrochemical method, using Tafel polarization and electrochemical impedance spectroscopy (EIS) techniques. The kinetic parameters and thermodynamic parameters were calculated using Arrhenius theory and transition state t...
متن کاملFretting wear in self-piercing riveted aluminium alloy sheet
Fretting wear in aluminium alloy AA5754 joined by self-pierce riveting (SPR), a relatively new fastening technique increasingly used in vehicle structures, has been investigated in this paper. Surface damages have been induced when a joint experienced a sinusoidal cyclic tension-tension load. Various degradation zones have been characterised in the contact surfaces between the aluminium sheets,...
متن کاملExtrusion of 7075 aluminium alloy through double-pocket dies to manufacture a complex profile
Low-temperature incipient melting and high deformation resistance of aluminium alloy AA7075 place extraordinary demands on extrusion die design and process optimization, especially when the shape of the extrudate is complex. The present case study was aimed at combining the considerations on die design and process optimization for the alloy to manufacture a complex solid profile with large diff...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Bio- and Tribo-Corrosion
سال: 2016
ISSN: 2198-4220,2198-4239
DOI: 10.1007/s40735-016-0042-3