Black GaAs by Metal-Assisted Chemical Etching
نویسندگان
چکیده
منابع مشابه
GaAs pillar array-based light emitting diodes fabricated by metal-assisted chemical etching
We demonstrate GaAs pillar array-based light emitting diodes (LEDs) with axial p-in junctions fabricated using a room-temperature metal-assisted chemical etching (MacEtch) method. Variations in vertical etch rates for all three doping types of GaAs are investigated as a function of etching temperature, oxidant/acid concentration ratio, and dilution of the etching solution. Control over nanopill...
متن کاملAu-Capped GaAs Nanopillar Arrays Fabricated by Metal-Assisted Chemical Etching
GaAs nanopillar arrays were successfully fabricated by metal-assisted chemical etching using Au nanodot arrays. The nanodot arrays were formed on substrates by vacuum deposition through a porous alumina mask with an ordered array of openings. By using an etchant with a high acid concentration and low oxidant concentration at a relatively low temperature, the area surrounding the Au/GaAs interfa...
متن کاملFormation of high aspect ratio GaAs nanostructures with metal-assisted chemical etching.
Periodic high aspect ratio GaAs nanopillars with widths in the range of 500-1000 nm are produced by metal-assisted chemical etching (MacEtch) using n-type (100) GaAs substrates and Au catalyst films patterned with soft lithography. Depending on the etchant concentration and etching temperature, GaAs nanowires with either vertical or undulating sidewalls are formed with an etch rate of 1-2 μm/mi...
متن کاملMetal-assisted chemical etching using sputtered gold: a simple route to black silicon.
We report an accessible and simple method of producing 'black silicon' with aspect ratios as high as 8 using common laboratory equipment. Gold was sputtered to a thickness of 8 nm using a low-vacuum sputter coater. The structures were etched into silicon substrates using an aqueous H2O2/HF solution, and the gold was then removed using aqua regia. Ultrasonication was necessary to produce columna...
متن کاملHierarchical silicon nanostructured arrays via metal-assisted chemical etching
Department of Physics and Materials Scien Chee Avenue, Kowloon Tong, Kowloon, Hon Department of Biology and Chemistry, Cit Avenue, Kowloon Tong, Kowloon, Hong Kon Centre for Functional Photonics (CFP), Cit Avenue, Kowloon Tong, Kowloon, Hong Kon Shenzhen Research Institute, City Universit † Electronic supplementary informa 10.1039/c4ra06172a ‡ These authors contributed equally to th Cite this: ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ACS Applied Materials & Interfaces
سال: 2018
ISSN: 1944-8244,1944-8252
DOI: 10.1021/acsami.8b10370