Mechanical and Thermal Properties of Chemically Modified Epoxy Resin
Diglycidyl ether of bisphenol-A (DGEBA), having number average molecular weight (Mn) 375, was modified by incorporating the hydroxyl terminated polybutadiene (HTPB) based prepolymer using isophorone diisocyanate as a coupling agent. To increase the compatibility between the epoxy resin and HTPB part, polar groups were introduced in the later to achieve physical and chemical interactions between...
متن کاملTrifunctional Epoxy Resin Composites Modified by Soluble Electrospun Veils: Effect on the Viscoelastic and Morphological Properties
Electrospun veils from copolyethersulfones (coPES) were prepared as soluble interlaminar veils for carbon fiber/epoxy composites. Neat, resin samples were impregnated into coPES veils with unmodified resin, while dry carbon fabrics were covered with electrospun veils and then infused with the unmodified epoxy resin to prepare reinforced laminates. The thermoplastic content varied from 10 wt% to...
متن کاملDevelopment of ricehusk ash reinforced bismaleimide toughened epoxy nanocomposites
Recent past decades have witnessed remarkable advances in composites with potential applications in biomedical devices, aerospace, textiles, civil engineering, energy, electronic engineering, and household products. Thermoset polymer composites have further enhanced and broadened the area of applications of composites. In the present work epoxy-BMI toughened-silica hybrid (RHA/DGEBA-BMI) was pr...
متن کاملPreparation and Characterization of a Novel Biodegradable Epoxy Resin Modified with Epoxidized Oleic Acid
The goal of this research was to study the curing behavior and biodegradability DER 736 modified with epoxidized oleic acid. In this paper we demonstrate the efficient epoxidation of oleic acid with performic acid generated in situ from formic acid and hydrogen peroxide in the presence of H2SO4 as catalyst. The highest relative epoxy yield of 61% was achieved at 40 ͦC after 10 h. DER 736 modifie...
متن کاملImpact Resistance Enhancement by Adding Core-Shell Particle to Epoxy Resin Modified with Hyperbranched Polymer
A core-shell particle was fabricated by grafting amino-terminated hyperbranched polymer to the surface of silica nanoparticles. The influences of core-shell particle contents on the tensile and impact strength of the epoxy thermosets modified with amino-terminated hyperbranched polymer were discussed in detail. For comparison, core-shell particle was added into the epoxy/polyamide system for to...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: KOBUNSHI RONBUNSHU
سال: 1992
ISSN: 0386-2186,1881-5685
DOI: 10.1295/koron.49.213