Bearing Failures of Pin Jointed CSM Laminates under Biaxial Loading
نویسندگان
چکیده
منابع مشابه
Peridynamic modeling of composite laminates under explosive loading
High velocity impact and shock or blast responses are a critical design characteristic determining sizing of composite parts and, ultimately, weight savings. This study demonstrates the applicability of peridynamics to accurately predict nonlinear transient deformation and damage behavior of composites under shock or blast types of loadings due to explosions. The peridynamic predictions correla...
متن کاملFailure of Fibrous Composite Plates under Static Biaxial Planar Loading
This paper outlines an experimental investigation carried out for the analysis of failure mechanisms in fibrous laminated composite plates containing stress raisers, in the form of cutouts, under static biaxial planar compressive loadiing. A specially designed biaxial loadiing frame was used to test a series of 48 ply graphite/epoxy composite laminated plates with centrally located circular hol...
متن کاملExperimental study on effect of loading rate on mode I delamination of z-pin reinforced laminates
This paper presents an experimental investigation on mode I delamination of z-pinned double-cantilever-beams (DCB) and associate z-pin bridging mechanisms. Tests were performed with three types of samples: big-pin with an areal density of 2%, small-pin with an areal density of 2% and small-pin with an areal density of 0.5%. The loading rates for each type of samples were set at 1 mm/min and 100...
متن کاملPrediction of Crack Initiation Direction for Inclined Crack Under Biaxial Loading by Finite Element Method
This paper presents a simple method based on strain energy density criterion to study the crack initiation angle by finite element method under biaxial loading condition. The crack surface relative displacement method is used to eliminate the calculation of the stress intensity factors which are normally required. The analysis is performed using higher order four node quadrilateral element. The...
متن کاملCracking of Laminates Subjected to Biaxial Tensile Strains
During the processing of laminar ceramic, biaxial, residual stresses can arise due to differential thermal contraction between unlike layers. A tensile stress can cause pre-existing flaws to extend across the layer and into the adjacent layers and then tunnel until they meet either another crack or a free surface. A previous analysis has shown that for a given residual stress there is a critica...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advanced Composites Letters
سال: 1995
ISSN: 2633-366X,2633-366X
DOI: 10.1177/096369359500400204