Atom Probe Tomography Studies of the Initiation of Localized Corrosion in Aluminum Alloy 2024
نویسندگان
چکیده
منابع مشابه
Crack Behavior of the Aluminum Alloy 2024 Under Fretting Conditions
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...
متن کاملA Galvanic Corrosion Approach to Investigating Chromate Effects on Aluminum Alloy 2024-T3
The effects of chromate treatment on the corrosion of an aluminum/copper aircraft alloy were examined with a galvanic corrosion apparatus composed of two electrodes and a zero resistance ammeter. Combinations of pure Al, pure Cu, and AA2024-T3 electrodes were immersed in 0.1 M NaCl solution, which was saturated with air, O2 , or argon. Selection of electrode material or differential aeration re...
متن کاملThe Inhibition of Sodium Oleate for Pitting Corrosion of Aluminum Alloy 2024 in 0.1 mol L-1 NaCl Solution
The inhibition mechanism of sodium oleate (C17H33COONa) for pitting corrosion of aluminum alloy (AA) 2024 in 0.1 mol L NaCl solution was investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), scanning electron microscopy with energy dispersive spectrometer (SEM-EDS) and X-ray photoelectron spectroscopy (XPS). C17H33COONa showed good inhibition effect on u...
متن کاملEffect of Aging Condition on Semisolid Cast 2024 Aluminum Alloy
2024 Aluminum alloy was squeezed cast by the Gas Induced Semi Solid (GISS) process. Effect of artificial aging on microstructure and mechanical properties of this alloy was studied in the present work. The solutionized specimens were aged hardened at temperatures of 175°C, 200°C, and 225°C under various time durations. The highest hardness of about 77.7 HRE was attained from specimen aged at th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Microscopy and Microanalysis
سال: 2017
ISSN: 1431-9276,1435-8115
DOI: 10.1017/s1431927617004147