Antibacterial Zinc Oxide Nanoparticle Coating of Polyester Fabrics
نویسندگان
چکیده
منابع مشابه
Antibacterial Zinc Oxide Nanoparticle Coating of Polyester Fabrics
Polyester knitted fabrics have been equipped with antibacterial properties by coating with aqueous suspensions of zinc oxide (ZnO) with different particle diameters. It can be shown that the antibacterial efficacy against Staphylococcus aureus and Klebsiella pneumonia and the permanence of the coating after defined washing cycles depends on the composition of the ZnO dispersion. To improve the ...
متن کاملEvaluation of Antibacterial Efficacy of Biogenic Zinc Oxide Nanoparticles on Cotton Fabrics
Growing need of potent antibacterial agents has renewed a keen interest in the development of nanomaterials with antibacterial properties. The current work demonstrated the biosynthesis of zinc oxide nanoparticles (ZnO NPs) using aqueous leaf extract of Cardiospermum halicacabum and its bactericidal activity. The resultant biogenic metal oxide nanoparticles were analyzed by various characteriza...
متن کاملSurface Modification of Polyester Fabrics with Vinyltriethoxysilane
Surface modification of polyester fabrics was studied aiming at improving the water repellency property. Vinyltriethoxysilane (VTES) was employed as surface modifying agent. Prior to application, VTES was prepared in aqueous emulsion using cetyltrimethylammoniun bromide (CTAB) as an emulsifying agent. The application of VTES emulsion was carried out using a padder and followed by curing at 150C...
متن کاملEffect of Chitosan, Aluminum Oxide and Silver Nanoparticles on Antibacterial, Deodorizing and Moisture Absorption Properties of Nonwoven Polyester Fabrics for Use in Medical Textiles
ABSTRACT Background and Objective: Hospital clothing and textiles have a great role in providing medical services to patients. Hospital services would not be possible without using these textiles. The aim of this study was to prepare non-woven polyester for use in medical textiles. Methods:...
متن کاملAnticorrosive Performance of Polyester–melamine Coating Fortified with Zinc Ferrite Nanoparticles
In this study, nanoparticle zinc ferrites with different particle sizes were synthesized via sol-gel method using ferric nitrate and zinc nitrate. The obtained gel was dried and calcined at three different temperatures (i.e. 500, 600 and 800 °C) for 2 h. Adequate amounts of the as-synthesized nanoparticle samples were then added to the mixture of polyester resin and formaldehyde resin. The ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Textile Science and Technology
سال: 2015
ISSN: 2379-1543,2379-1551
DOI: 10.4236/jtst.2015.12007