Antibacterial TaC-(Fe,Cr,Mo,Ni)-(Ag/Cu) Composite Coatings with High Wear and Corrosion Resistance in Artificial Seawater
نویسندگان
چکیده
The synergistic effect of simultaneous mechanical wear, chemical/electrochemical corrosion (tribocorrosion) and microbial attack poses a serious threat to marine coastal infrastructure. To address this important problem, we have developed composite coatings consisting TaC (25–35 at.%) corrosion-resistant α-Fe(Cr,Ni,Mo)-based metal matrix, as well bactericidal elements (Cu, Ag). Coatings 50–75 μm thick were obtained by electrospark deposition in vacuum. possess high hardness (up 10 GPa) resistance cyclic dynamic loads compared with the stainless steel (SS) substrate. Tribocorrosion experiments showed that decrease potential associated removal passivating film from surface during friction was 2–2.5 times smaller for Ag-containing coating than other tested materials. material passivation rates also different: almost instantaneous Ag- Cu-doped coatings, slow several minutes Ag/Cu-free SS. shows lowest coefficient (0.2–0.25) minimal wear rate (1.6 × 10−6 mm3/Nm) artificial seawater. Ag-doped exhibits most positive value current density. After exposure seawater 20 days, only no signs pitting corrosion. All studied materials pronounced against Bacillus cereus Arc30 bacteria. resulting can be used protect products tribocorrosion fouling
منابع مشابه
Thermal Sprayed Coatings Used Against Corrosion and Corrosive Wear
Coatings have historically been developed to provide protection against corrosion and erosion that is to protect the material from chemical and physical interaction with its environment. Corrosion and wear problems are still of great relevance in a wide range of industrial applications and products as they result in the degradation and eventual failure of components and systems both in the proc...
متن کامل"tin Coatings for Wear Resistance and Gold-like Decorative Coatings"
Titanium Nitride (TiN) coatings have led the way for providing increased wear resistance and extended life of cutting tools, whether carbide inserts or high-speed steel. Where the earliest applications were for high temperature substrate materials (carbides) and chemical vapor deposition (CVD) was the process of choice, later developments in the physical vapor deposition (PVD) technology, espec...
متن کاملLaboratory evaluation of composite wear resistance with and without occlusal index
Laboratory evaluation of composite wear resistance with and without occlusal index Dr. MJ. Moghadas * - Dr. N. Sarabi * - Dr. H. Ameri * - Dr. A. Salehi** *Assistant Professor of Operative Dentistry Dept., Faculty of Dentistry, Mashhad University of Medical Sciences. ** Dentist. Abstract Background and Aim: The polishing and finishing procedures may cause topographical changes and introduce sub...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Lubricants
سال: 2022
ISSN: ['2075-4442']
DOI: https://doi.org/10.3390/lubricants10110320