Anti-infective coatings for titanium implants by alternating current electrophoretic deposition
نویسندگان
چکیده
منابع مشابه
New anti-infective coatings of medical implants.
Implantable devices are highly susceptible to infection and are therefore a major risk in surgery. The present work presents a novel strategy to prevent the formation of a biofilm on polytetrafluoroethylene (PTFE) grafts. PTFE grafts were coated with gentamicin and teicoplanin incorporated into different lipid-like carriers under aseptic conditions in a dipping process. Poly-d,l-lactic acid, to...
متن کاملAlternating Current Electrophoretic Deposition of Antibacterial Bioactive Glass-Chitosan Composite Coatings
Alternating current (AC) electrophoretic deposition (EPD) was used to produce multifunctional composite coatings combining bioactive glass (BG) particles and chitosan. BG particles of two different sizes were used, i.e., 2 μm and 20-80 nm in average diameter. The parameter optimization and characterization of the coatings was conducted by visual inspection and by adhesion strength tests. The op...
متن کاملTitanium Oxide (TiO2) Coatings on NiTi Shape Memory Substrate Using Electrophoretic Deposition Process
The aim of the present research is to convert bioinert surface of NiTi to bioactive and biocompatible surface. In order to develop a bioactive and corrosion resistant film on NiTi, electrophoretic deposition process was done and TiO2 particles were deposited on the NiTi surface. Suspensions including TiO2 particles were prepared using a mixture of acetone and n-butanol (0%, 30%, 60%, 80% and 10...
متن کاملNovel Bioactive Antimicrobial Lignin Containing Coatings on Titanium Obtained by Electrophoretic Deposition
Hydroxyapatite (HAP) is the most suitable biocompatible material for bone implant coatings; its brittleness, however, is a major obstacle, and the reason why research focuses on creating composites with biopolymers. Organosolv lignin (Lig) is used for the production of composite coatings, and these composites were examined in this study. Titanium substrate is a key biomedical material due to it...
متن کاملSurface modification for titanium implants by hydroxyapatite nanocomposite
Background: Titanium (Ti) implants are commonly coated with hydroxyapatite (HA). However, HA has some disadvantages such as brittleness, low tensile strength and fracture toughness. It is desirable to combine the excellent mechanical properties of ZrO2 and the chemical inertness of Al2O3 with respect to the purpose of this project which was coating Ti implants with HA-ZrO2-Al2O3 to modify the s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Frontiers in Bioengineering and Biotechnology
سال: 2016
ISSN: 2296-4185
DOI: 10.3389/conf.fbioe.2016.01.02118