Nanotwins Formation in Accumulative Roll-Bonded Brass
Accumulative roll-bonding (ARB) is a severe plastic deformation process that is using rolling to produce ultrafine grains in coarse grained metallic materials. In this study, ARB has been applied on 70/30 brass up to 6 cycles at ambient temperature and non-lubricated conditions to apply a true strain up to 4.8 Von Mises strain. Microstructures of ARBed brass samples were characterized by scanni...
متن کاملAnnealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding
Ultrafine grained sheets were prepared from a twin-roll cast AA8006 aluminium alloy using accumulative roll-bonding process at room temperature. The evolution of microstructure of sheets after three accumulative roll-bonding passes during isochronal annealing with a constant step of 20 °C/20 min was studied by light and electron microscopy. The influence of the resulting microstructure on mecha...
متن کاملFriction stir welding of accumulative roll bonded single phase brass
Single phase brass strips with 2 mm thickness were severely deformed through 1 and 3 cycles of accumulative roll bonding process (ARB). ARB process effectively increased the hardness, yield strength, and the ultimate strength of the processed materials. The hardness of processed material increased from 95 HV in annealed material to 225 HV in 3 cycle ARBed material, and the yielding and ultimate...
متن کاملnanotwins formation in accumulative roll-bonded brass
accumulative roll-bonding (arb) is a severe plastic deformation process that is using rolling to produce ultrafine grains in coarse grained metallic materials. in this study, arb has been applied on 70/30 brass up to 6 cycles at ambient temperature and non-lubricated conditions to apply a true strain up to 4.8 von mises strain. microstructures of arbed brass samples were characterized by scanni...
متن کاملAccumulative Roll Bonding of Aluminum/Stainless Steel Sheets
An Al/Stainless Steel/Al lamellar composite was produced by roll bonding of the starting sheets at 400 °C. Afterward, the roll bonded sheet was cut in half and the accumulative roll bonding (ARB) process at room temperature was applied seven times. As a result, the central steel layer fractured and distributed in the Al matrix among different layers introduced by the repetition of roll bonding ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Sciences
سال: 2019
ISSN: 2076-3417
DOI: 10.3390/app9173627