A notch stress method for fatigue life prediction of spot-welded joints
نویسندگان
چکیده
منابع مشابه
Fatigue Life Prediction for Welded Joints with Known Initial Crack
The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملFatigue Life Assessment of Welded Joints Considering Crack Propagation Based on Hot Spot Stress
In this study, fatigue test and crack propagation analysis of welded joints in ships and offshore structures were performed. The test models have two types of welded joints, T-joint and double plate. Test data is presented in S-N curves obtained by the Hot Spot Stress (HSS) approach. The S-N data for each length of crack were appraised to define the fatigue life of crack initiation and propagat...
متن کاملFatigue Life Prediction of Rivet Joints
Strength reduction in structures like an aircraft could be resulted as cyclic loads over a period of time and is an important factor for structural life prediction. Service loads are emphasized at the regions of stress concentration, mostly at the connection of components. The initial flaw prompting the service life was expected by using the Equivalent Initial Flaw Size (EIFS) which has been re...
متن کاملFatigue Strength Assessment of Welded Joints by Using Notch Stress Approach
The fatigue strength assessment of welded joints by using the known parent material fatigue strength is considered in this paper. The stress concentration factor was determined performing FEA of singlesided transverse attachment joints for mean value of weld toe radius which was calculated by using several measurements of the weld toe radius along the weld length. The fatigue strength of welded...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2019
ISSN: 2261-236X
DOI: 10.1051/matecconf/201930019003