A Ductile Tear Fracture Analysis of Lap Welded Joints
نویسندگان
چکیده
منابع مشابه
Seam-Tracking for Friction Stir Welded Lap Joints
This article presents a method for automatic seam-tracking in friction stir welding (FSW) of lap joints. In this method, tracking is accomplished by weaving the FSW tool back-and-forth perpendicular to the direction of travel during welding and monitoring force and torque signals. Research demonstrates the ability of this method to automatically track weld seam positions. Additionally, tensile ...
متن کاملFatigue Behaviour Study of Laser Hybrid Welded Eccentric Fillet Joints – Part Ii: State-of-the-art of Fracture Mechanics and Fatigue Analysis of Welded Joints
Simplified fatigue and fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineering components under normal and abnormal service loads. In many cases, welded joints are the regions most likely to contain original fabricatio...
متن کاملFracture mechanics-based life prediction of a riveted lap joint
In this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. Simulation results showed that mode I was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. Afterward, the fract...
متن کاملA Numerical Study of the Ductile Tearing in Welded Joints Using the Rice-Tracey Void Growth Model
A finite element (FE) analysis of a CT25 specimen has been achieved for three configurations of a welded structure : monometallic (base metal), bimetallic (base metal and weld metal) and trimetallic (BM+WM+HAZ). Using the RICE-TRACEY model, a void growth parameter R& has been computed for each case. The evolution of this parameter indicates clearly that the bimetallic specimen is the most h d w...
متن کاملFatigue behaviour of composite adhesive lap joints
This paper is concerned with a fatigue study of composite adhesive lap joints produced from a bi-directional woven E-glass fibres and polypropylene. The adhesive used was a Bostik 7452 (Rubber & Plastics Grade) ethyl cyanoacrylate type. The effects of layer orientation, lap joint length and water immersion on the fatigue behaviour were studied. The specimens were immersed in water during period...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Strength of Materials
سال: 2004
ISSN: 0039-2316
DOI: 10.1023/b:stom.0000041539.84799.7c