In this work, nanocrystalline Fe85Si10Ni5 soft magnetic powders were prepared by mechanical alloying and subsequent annealing to reduce the internal stresses and lattice strains. The powders were mixed with phenolic resin and warm pressed to produce nanostructured soft magnetic composites. The effect of annealing time and temperature on the crystalline structure, microstructure and magnetic pro...

Abstract There are various methods to produce iron based nano crystalline magnetic alloys. Among these methods, mechanical alloying is one of the most important. In this research, nano crystalline Fe85Si10Ni5 soft magnetic alloy was synthesized by mechanical alloying. The effect of alloying time on phase constituents and magnetic properties of the produced powders was investigated, by X-ray di...

Nanocrystalline strontium hexaferrite (SrFe12O19) powders have been successfully synthesized using the facile Co-precipitation method. The ferrite precursors were achieved from mixtures of strontium and ferric chloride in an aqueous medium without any surfactant and soft template. The as-received powders were calcined at 800 and 1000 ˚C for 2 hours in air. The final powders were characterized b...

In this research, electroplated magnetically isotropic and anisotropic soft alloys and screen-printed soft ferrites applicable to micromachined micromagnetic devices are fabricated and characterized using in situ measurement techniques. Appropriate magnetic materials and deposition methods, such as electroplating and screen-printing techniques, are examined and material test structures are fabr...

Additive manufacturing (AM) allows printing parts of complex geometries that cannot be produced by standard technologies. Besides, AM provides the possibility to create gradient materials with different structural and physical properties. We, for first time, printed soft magnetic from paramagnetic powders (316L steel Cu-12Al-2Fe (in wt.%) aluminium bronze)). The properties can adjusted during i...

A single phased Y-type hexagonal ferrite Sr2Co1.7Mg0.3Fe11.2Sn0.4Zn0.4O22 was synthesized by the sol–gel auto combustion method. Structural and magnetic properties of this composition of Y-type hexagonal ferrite have been investigated. The X-ray diffraction (XRD) patterns confirm single phase Y-type hexagonal ferrite and various parameters such as lattice constants and cell volume have been cal...

Nd2Fe14B/α-Fe-based hard/soft nanocomposite magnets with Co addition have been prepared by ball-milling and warm compaction. It was found that Co addition into the magnetically hard phase improves magnetic properties significantly, especially the remanence ratio and coercivity. The effect on the magnetic properties of the selective Co addition may be attributed to enhanced interdiffusion across...