expansive soils may cause disaster if not adequately taken care of. lime continues to be commonly used for modification of these types of soils although it may have limited success in some applications. thus, the present study was performed to address the viability of using silica fume (sf) as industrial waste to modify the behavior of expansive soils. this achieves the double objectives of ove...

This study focuses on the effect of the amount of silica fume addition and volume fraction of steel fiber on the engineering properties of cementitious materials. Test variables include dosage of silica fume (5% and 10%), water/cement ratio (0.35 and 0.55) and steel fiber dosage (0.5%, 1.0% and 2.0%). The experimental results included: compressive strength, direct tensile strength, splitting te...

Corrosion of steel is one of the most important potential dangers and threats in concrete structures. Corrosion of steel embedded in reinforced concrete plays a key role in reducing the strength and durability of reinforced concrete. Several studies have proposed that alternative approaches to enhancing the performance of reinforced concrete and its resistance to corrosion. In this study, the r...

This paper describes the low temperature synthesis of belite (β-C2S) from silica fume. Mixtures of lime, BaCl2, and silica fume with the ratio of (Ca + Ba)/Si = 2 were hydrothermally treated in stainless steel capsule at 110-150°C for 2-5 hours, calcined at 600-700°C for 3 hours, and analyzed by FTIR, XRD, TGA/DTA, and SEM techniques. Dicalcium silicate hydrate (hillebrandite) was prepared by h...

In the exploratory study presented in this paper, an attempt was made to develop different mixtures of ultrahigh performance concrete (UHPC) using various locally available natural and industrial waste materials as partial replacements of silica fume and sand. Materials such as natural pozzolana (NP), fly ash (FA), limestone powder (LSP), cement kiln dust (CKD), and pulverized steel slag (PSS),...

The tensile creep behavior is extremely important in crack prediction and stress analysis of concrete. The main objective is investigating the effects of the silica fume on the tensile basic creep of early-aged concrete. The effect of silica fume on tensile creep was studied using lever-type tensile creep tester. Silica fume amount by weight of total cementing material was 0%, 5%, 10% and 15%. ...

plastic shrinkage is one of the most important parameter which must be considered in hot weather concreting. if plastic shrinkage is not prevented, cracking will be significant, especialy if silica fume is used in the mix. in this paper, the effect of silica fume in bleeding and evaporation was investigated in laboratory. the results showed that in restrained shrinkage, beside relative humidity...

The addition of sand to cement paste was found to degrade the vibration damping ability, as shown by decreases in both loss tangent and storage modulus under flexure. However, further addition of silica fume more than restored the vibration damping ability, due to the silica fume causing increases in both loss tangent and storage modulus. Silica fume increased the loss modulus of mortar by as m...

this paper deals with the interfacial effects of silica fume (sf) and styrene-butadiene polymer (sbr) on compressive strength of concrete. analyzing the compressive strength results of 32 concrete mixes performed over two water-binder ratios (0.35, 0.45), four percentages replacement of silica fume (0%, 5%, 7.5%, 10%) and four percentages of sbr (0%, 5%, 10%, 15%) were investigated. a mathemati...

Microsilica, or silica fume, is an amorphous type of silica mostly collected as byproduct of the silicon and ferrosilicon alloy production. In this work, low shrinkage alumina-mullite ceramic composites were prepared from mixtures of calcined alumina, silica fume and aluminum metal powder and sintered at 1550 o C for 2 hrs. The influence of silica fume and aluminum powder on the densification p...