in this research work, it was planned to study influences of hydrothermal treatment temperature, holding time and press temperature on wood density, spring back, moisture absorption as well as dimensional stability of combined-hydro-thermo-mechanically modified poplar wood. wood blocks were treated hydrothermally at temperatures 120, 150 and 180°c for holding time of 0, 30 and 90 min. afterward...

Beeswax was modified through the direct blending of nano-TiO₂, chitosan, acid dyes, and neutral dyes. With the varied modified beeswax, hot waxing was conducted on compressed poplar wood. Treated wood surfaces were characterized with scanning electron microscopy and thermogravimetric analysis. Results show that the C, O, N, Au, S, and Ti elements in modified beeswax successfully penetrated into...

Thermal modifications tend to darken wood color and enhance dimensional stability, erosion resistance, weather resistance, and product value. To investigate the chemical characteristics of VOCs influenced by the heat treatment process, air-dried poplar wood was heat-treated at four treatment temperatures (160,180, 200, and 220 °C) for 2 h. Near-infrared spectroscopy (NIR) was used to investigat...

Oil heat treatment can effectively improve the dimensional stability and bio-durability of wood. However, the characteristics of high oil uptake (50 percent or higher) and high susceptibility to leaching from wood have an adverse effect on subsequent manufacturing processes of wood product and production costs. A solvent extraction (100% ethanol) process was used to extract the surplus oil from...

One of the most persistent problems with mechanically densified wood is its inherent dimensional instability. The effects of heat post-treatment on the changes in spring-back (SB), compression ratio recovery (CRR), thickness swelling (TS), and water absorption (WA) of newly-tested Uludağ fir (Abies bornmuelleriana Mattf.) and black poplar (Populus nigra L.) wood samples that had been thermo-mec...

in this study, compressed poplar wood was used to improve the strengths of wooden chairs. these chairs were compared to chairs made from uncompressed poplar wood. wooden chairs were assembled with two types of traditional joints including mortise and tenon and wooden pins joints. the ultimate force was applied from the front to the back of the seat, were recorded according to american library a...

The objective of this study was to quantify the influence of zinc oxide nanoparticles (nanoZnO) on the water repellency and dimensional stability of beech wood. Beech wood blocks were treated with a nano-ZnO solution at four treatment levels (0, 10,000, 20,000, and 40,000 ppm) using a modified dip method. Also, a thermal treatment was performed at 60 and 120°C. After conditioning the samples, w...

Fast-growing poplar wood was modified with low molecular weight ureaformaldehyde resin (UF) at 41.5% concentration or phenol-formaldehyde (PF) at concentrations of 15, 25, and 40%. The physical and mechanical properties were measured, and creep behavior tests were carried out under ambient indoor conditions. The specimens were subjected to 30 and 50% of their maximum bending load. The density, ...

This study evaluates the edgewise bending moment capacity of the four most frequently used middle joints in the upholstered furniture frames. The research included the following joints: Mortise and Tenon, double Dowel, Corner Blocks and double Gusset Plates, designed in the form of middle joints and made of beech and poplar solid wood. The test results indicated that regarding the edgewise bend...