fire-retarding properties of wollastonite nanofibers in poplar wood (populus nigra) were studied here. some physical properties such as water absorption, volumetric swelling and anti-swelling efficiency (ase) were also measured. specimens were prepared according to the iso 11925 specifications for the fire-retarding properties and according to the astm d4446 -2002 specifications for the physica...

Fire-retarding properties of wollastonite nanofibers in poplar wood (Populus nigra) were studied here. Some physical properties such as water absorption, volumetric swelling and anti-swelling efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 specifications for the fire-retarding properties and according to the ASTM D4446 -2002 specifications for th...

Fire-retarding properties of wollastonite nanofibers in poplar wood (Populus nigra) were studied here. Some physical properties such as water absorption, volumetric swelling and anti-swelling efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 specifications for the fire-retarding properties and according to the ASTM D4446 -2002 specifications for th...

Effects of heat-transferring property of silver nanoparticles were evaluated on two solid woods of poplar and fir and in combination with Borax. Nanosilver and Borax were applied in pressure vessel using Rueping method. The size range of silver nanoparticles was 20-80 nm. Specimens of 150×130×9 mm were prepared and five fire-retarding properties were measured using a newly designed slide fire t...

Effects of heat-transferring property of silver nanoparticles were evaluated on two solid woods of poplar and fir and in combination with Borax. Nanosilver and Borax were applied in pressure vessel using Rueping method. The size range of silver nanoparticles was 20-80 nm. Specimens of 150×130×9 mm were prepared and five fire-retarding properties were measured using a newly designed slide fire t...

effects of heat-transferring property of silver nanoparticles were evaluated on two solid woods of poplar and fir and in combination with borax. nanosilver and borax were applied in pressure vessel using rueping method. the size range of silver nanoparticles was 20-80 nm. specimens of 150×130×9 mm were prepared and five fire-retarding properties were measured using a newly designed slide fire t...