This study evaluated the effect of different types of filler in a resin-based pit and fissure sealant on fluoride release, recharge, and lactic acid neutralization. Resin-based sealant was incorporated with 5% w/w of the following fillers: calcium aluminate cement (CAC), synthesized mesoporous silica (SI), a CAC and SI mixture (CAC+SI), glass-ionomer powder (GIC), and acetic acid-treated GIC (G...

calcium aluminates (ca) are the most important hydraulically setting cements used for preparing refractory castables, because they develop high strength at very early ages after placements.  the anhydrous phases of this kind of cements are ca, ca2 and traces of c12a7 and alpha-alumina. the major hydraulic phase in all of the ca cements including ciment fondue is ca. once hydrated, it starts to ...

Citric acid added as set retarder significantly contributed to enhancing the setting temperature and to extending the thickening time of a calcium aluminate phosphate (CaP) geothermal cement slurry consisting of calcium aluminate cement (CAC) as the base reactant and sodium polyphosphate (NaP) solution as the acid reactant. The set-retarding activity of citric acid was due to the uptake of Ca2'...

The effect of pseudowollastonite (Pw) additions on the in vitro bioactivity and compressive strength of composites based on calcium aluminate cement (CAC) was studied. Composites were prepared by mixing calcium aluminate clinker with pseudowollastonite (5 and 10 wt%) at a w/c ratio of 0.4 (0.015M LiCl aqueous solution). In order to assess the in vitro bioactivity and compressive strength, compo...

Calcium aluminate cement (CAC) suffers from loss of workability in less than an hour (~15 minutes) after first touch of water. Current superplasticizers that are utilized to modify the viscosity of cement admixtures are designed to target ordinary Portland cement (OPC). The high affinity between these superplasticizers and cement particles were found to be detrimental in CAC systems. Utilizatio...

The purpose of this study was to evaluate the physical properties and hydration evolution of calcium aluminate cement (CAC) compositions containing an advanced dispersant. The compressive strength, dimensional change, apparent porosity and quantitative X ray diffraction analysis (XRD) of the cement pastes were carried out over 1-15 days of curing (with the samples immersed in distilled water) a...

in this work, we studied the effect of carboxylic acid on the rheological properties of a high-alumina cement mortar (ch45) produced by the algerian firm refractal.the investigated properties are setting time, water consumption, electrical conductivity, ph, density and the compressive strength. the results show a setting time of about 200 min for the acid free, 180 min with 0.1 % of carboxylic ...

The present study concerns a development of calcium aluminate cement (CAC) concrete to enhance the durability against an externally chemically aggressive environment, in particular, chloride-induced corrosion. To evaluate the inhibition effect and concrete properties, CAC was partially mixed with ordinary Portland cement (OPC), ranging from 5% to 15%, as a binder. As a result, it was found that...

Cementing systems based on calcium aluminate cement (CAC) have been studied as an alternative cement matrix for the encapsulation of intermediate level wastes (ILW) arising from the nuclear industry. CAC-based systems have great potential for the incorporation of aluminium containing ILW owing to the near-neutral internal pH of these binders. However, CAC-based binders usually undergo phase con...