As one of the main products produced by oral microorganisms, the role of lactic acid in the corrosion of titanium is very important. In this study, the corrosion behavior of titanium in artificial saliva with and without lactic acid were investigated by open-circuit potentials (OCPs), polarization curves and electrochemical impedance spectroscopy (EIS). OCP firstly increased with the amount of ...

The performance of amino acids and carboxylic acids of biological importance on the corrosion of mild steel and copper in sodium chloridesolutionswas investigated. Manyofthe amino acidsare inhibitive. Aspartic acid, cysteine, cystine, threonine and histidine enhance the corrosion of mild steel. For copper, however, all t he compounds except 4-amino n-butyric acid and hippuric acid, promote corr...

The corrosion behavior of mild steel in the presence of acetic acid (CH3COOH) and carbon dioxide (CO2) has been investigated using electrochemical techniques and weight-loss measurements. Electrochemical measurements have shown that the presence of acetic acid affects predominantly the cathodic reaction. The acetic acid effect is much more pronounced at elevated temperatures when catastrophic c...

Corrosion inhibition of mild steel was studied using L-Dopa in aqueous hydrochloric acid and sulphuric acid solutions. The corrosion behaviours of the steel specimen in the presence of inhibitor weret studied by galvanostatic polarization and weight loss techniques. The measured electrochemical data indicated good inhibition of corrosion in both the corrosive medium in presence of L-DOPA. The c...

Problem statement: The effect of different temperatures and acid concentrations on the corrosion of low carbon steel in hydrochloric acid were addressed in this study. Approach: The effect of temperature was explained by application of Arrhenius equation and transition state theory, while the acid concentration effect was explained using reaction kinetic equations. The combined effect of temper...

The expense of repair and maintenance of private and public sewage systems in Germany runs to about 100 billion US $. This primarily affects concrete pipes and brickwork sewers. Approximately 40 per cent of the damage can be attributed to corrosion by biogenous sulfuric acid attack as a result of long flow periods and insufficient ventilation of waste water. The report deals with investigations...

Borated water leakage through spent fuel pools (SFPs) at pressurized water reactors is a concern because it could cause corrosion of reinforcement steel in the concrete structure and compromise the integrity of the structure. Because corrosion rate of carbon steel in concrete in the presence of boric acid is lacking in published literature and available data are equivocal on the effect of boric...

The carbon dioxide corrosion electrochemistry of mild steel has been studied in the presence of high CO2 partial pressures and acetic acid (HAc). Potentiodynamic sweeps, linear polarization resistance (LPR) and weight loss (WL) experiments have been conducted to investigate the effects of flow velocity, CO2 partial pressure, and acetic acid concentration on the corrosion rate of mild steel. Ele...

Background: This study investigated the prevention of stack corrosion under wet flue gas desulfurization conditions in a coal-fired power plant. The performance analysis and comparative studies of six materials for the prevention of stack corrosion were investigated. Results: The ion chromatography analysis showed the acid condensation contained fluoride, chloride, nitrate, sulphate, and sulphi...