Magnesium and its alloys--a new class of degradable metallic biomaterials-are being increasingly investigated as a promising alternative for medical implant and device applications due to their advantageous mechanical and biological properties. However, the high corrosion rate in physiological environments prevents the clinical application of Mg-based materials. Therefore, the objective of this...

Equal channel angular pressing (ECAP) was performed on ZK60 alloy and pure Mg in the temperature range 150-250 °C. A significant grain refinement was detected after ECAP, leading to an ultrafine grain size (UFG) and enhanced formability during extrusion process. Comparing to conventional coarse grained samples, fracture elongation of pure Mg and ZK60 alloy were significantly improved by 130% an...

The microstructure and mechanical properties of butt-joints produced by linear friction stir welding similar plates as-cast ZK60 modified with 1.5 wt.% RE (ZK60–1.5RE) are investigated. thermomechanical affected zone is investigated in both advancing retrieving sides, the compared to base metal stirred zone. Electron backscattered diffraction measurements provide average microstructural feature...

This research work has been carried out to study the effect of different Ca contents (0.5, 1.0, 1.5, 2.0 and 3.0) on the microstructure and porosity content of ZK60 alloys. The samples were examined by using optical and scanning electron microscopy (SEM) to evaluate the modification efficiency of the alloy with different Ca concentrations. The cast specimens were modified, homogenized and extru...

Zinc and zirconium were selected as the alloying elements in biodegradable magnesium alloys, considering their strengthening effect and good biocompatibility. The degradation rate, hydrogen evolution, ion release, surface layer and in vitro cytotoxicity of two Mg-Zn-Zr alloys, i.e. ZK30 and ZK60, and a WE-type alloy (Mg-Y-RE-Zr) were investigated by means of long-term static immersion testing i...

In this paper, hydroxyapatite coating was successfully deposited on ZK60 magnesium alloy surface by ultrasound-assisted electrodeposition method, and the macroscopic structure, chemical composition corrosion properties of sample HA were analyzed. The results show that quality is improved ultrasonic power, uniform, smooth compact. XRD FTIR analysis main obtained assisted hydroxyapatite. treatmen...

This work introduces Mg-4Zn-3Gd-1Ca/2ZnO (wt.%) nanocomposite fabricated using the technique of disintegrated melt deposition and extrusion. Addition of ZnO nanoparticles enhanced the compressive strengths of alloy by ~100 MPa. Nanocomposite samples display high strength and good ductility: 0.2% compressive yield stress of 355 MPa, ultimate compressive stress of 703 MPa, and compressive failure...