this paper provides an overview on obtaining low-carbon ultra-fine grained dual-phase steels through rapid intercritical annealing of cold-rolled sheet as improved materials for automotive applications. a laboratory processing route was designed that involves cold-rolling of a tempered martensite structure followed by a second tempering step to produce a fine grained aggregate of ferrite and ca...

This paper provides an overview on obtaining low-carbon ultra-fine grained dual-phase steels through rapid intercritical annealing of cold-rolled sheet as improved materials for automotive applications. A laboratory processing route was designed that involves cold-rolling of a tempered martensite structure followed by a second tempering step to produce a fine grained aggregate of ferrite and ca...

in the present study, mechanical properties and low cycle fatigue behavior of a solid-solutionized aa6061 aluminum alloy produced by equal channel angular pressing (ecap) process were investigated. the grain refinement after two passes of ecap significantly increased the yield stress and ultimate tensile stress and decreased the ductility of the alloy. however, the improvement of low cycle fati...

in this study, ultrafine grained 2024 al alloy based b4c particles reinforced composite was produced by mechanical milling and hot extrusion. mechanical milling was used to synthesize the nanostructured al2024 in attrition mill under argon atmosphere up to 50h. a similar process was used to produce al2024-5%wt. b4c composite powder. to produce trimodal composites, milled powders were combined w...

A microstructure consisting of ultrafine grained (UFG) ferrite with average grain size of ~ 0.7 µm and dispersed nano-sized carbides was produced by cold-rolling and tempering of the martensite starting microstructure in a low carbon steel. Subsequently, fine grained dual phase (DP) steel consisting of equiaxed ferrite grains with average size of ~ 5 µm and martensite islands with average size ...

in this paper, an ultra low carbon high strength low alloy grade steel was subjected to a two-step forging processand this was followed by different post cooling methods. the highest strength was obtained at a faster coolingrate due to the highly dislocated acicular ferrite structure with the fine precipitation of microalloying carbides andcarbonitrides. at a slow cooling rate, the strength fel...

aisi 304l austenitic stainless steel with different grain sizes of 0.5 -12 μm was obtained through the martensiticprocess. corrosion behavior of different samples was investigated in a 0.5m hcl solution using open circuitpotential, potentiodynamic polarization and electrochemical impedance spectroscopy tests. also, the correlationbetween the grain size and pitting corrosion resistance was asses...

In this paper, an ultra low carbon High Strength Low Alloy Grade Steel was subjected to a two-step forging process and this was followed by different post cooling methods. The highest strength was obtained at a faster cooling rate due to the highly dislocated acicular ferrite structure with the fine precipitation of microalloying carbides and carbonitrides. At a slow cooling rate, the strength ...