Tribocorrosion in taper junctions of retrieved anatomic shoulder arthroplasty implants was evaluated. A comparison of the tribocorrosion between cobalt-chromium and titanium alloy stems was conducted and the observations were correlated with the individual's clinical data. Adverse effects caused by metal debris and subsequent elevated serum metal ion levels are frequently reported in total hip ...

Valuable insights into the wear-corrosion behavior of metals, as well as into the tribocorrosion field through the development of simulation models of tribocorrosion experiments, can contribute in rationalizing wearaccelerated experiments and their open circuit potential (OCP) behavior under rubbing. These results demonstrate that mathematical models of controlled tribo-electrochemical contacts...

In the present study, a forged CoCrMo (ISO 5832-12) has been subjected to pulsed plasma treatment in a N2/H2 atmosphere at low temperatures (below 500 C). This treatment resulted in the formation of a layer composed by dispersed chromium nitride particles in a N-enriched metal matrix. The materials were tested for corrosion and tribocorrosion performance in 0.9 wt% NaCl at room temperature unde...

Hafnium is a passive metal with good biocompatibility and osteogenesis, however, little is known about its resistance to wear and corrosion in biological environments. The corrosion and tribocorrosion behavior of hafnium and commercially pure (CP) titanium in simulated body fluids were investigated using electrochemical techniques. Cyclic polarization scans and open circuit potential measuremen...

A good biocompatibility, excellent mechanical properties and high corrosion resistance characterize CoCrMo alloys. Therefore they are widely used for artificial joints in biomedical implants. However, the degradation of the implants during service life leads to the release into the body of toxic ions and wear particles. This continuous degradation is of concern for long-term stability of the im...

TiN/SiOx duplex coatings were synthesized on AISI304 stainless steel by plasma immersion ion implantation and deposition (PIIID) followed by radio frequency magnetron sputtering (RFMS). The microstructure and tribocorrosion failure behaviors of the duplex coatings were investigated by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, atomic force microscopy, rec...

The corrosion and tribocorrosion behavior of an as-cast high carbon CoCrMo alloy immersed in phosphate buffered solution (PBS) and phosphate buffered solution with bovine serum albumin (PBS+BSA) have been analyzed by electrochemical techniques and surface microscopy. After the electrochemical characterization of the alloy in both solutions, the sample was studied tribo-electrochemically (by ope...

One of the biggest motivations behind the development of the metal matrix composites (MMCs) is the improvement of the mechanical wear resistance of the unreinforced metallic matrix material mainly by the load-bearing effect of the hard reinforcement phases. However, in a large number of applications, MMCs are also required to operate in intimate contact with aqueous environments, which may lead...

Degradation by wear and corrosion are frequently encountered in a variety of tribosystems, including materials tools forming operations. The combined effect corrosion, known as tribocorrosion, can result accelerated material degradation. Interfacial conditions affect this Tribocorrosion maps serve the purpose identifying operating at interface for an acceptable rate This paper proposes machine ...