Conventional material removal of BK7 optical glass will normally result in brittle fracture at the surface, generating severe subsurface damage and poor surface finish. Subsurface damages induced by grinding strongly influence the mechanical strength and optical quality of optical glasses. However, through ductile mode grinding it is possible to reduce the surface and subsurface cracks. It is m...

Micro cracks occurring in concrete around tensile rebar is well known latent damage phenomenon. These micro cracks develop, and can be detected after reaching the surface of the concrete. Detection of these cracks before they are fully formed is preferable, but observing the whole crack structure is difficult. Another problem is repairing micro cracks under the concrete surface. The autogenous ...

Conventional material removal of BK7 optical glass will normally result in brittle fracture at the surface, generating severe subsurface damage and poor surface finish. Subsurface damages induced by grinding strongly influence the mechanical strength and optical quality of optical glasses. However, through ductile mode grinding it is possible to reduce the surface and subsurface cracks. It is m...

Solidification cracking is a key phenomenon associated with defect formation during welding. To elucidate the failure mechanisms, solidification cracking during arc welding of steel are investigated in situ with high-speed, high-energy synchrotron X-ray radiography. Damage initiates at relatively low true strain of about 3.1% in the form of micro-cavities at the weld subsurface where peak volum...

Effective elastic properties of a defected solid with distributed cohesive micro-cracks are estimated based on homogenization of the Dugdale–Bilby–Cottrell–Swinden (Dugdale–BCS) type micro-cracks in a two dimensional elastic representative volume element (RVE). Since the cohesive micro-crack model mimics various realistic bond forces at micro-scale, a statistical average of cohesive defects can...

A homogenous TiO2 / multi-walled carbon nanotubes(MWCNTs) composite film were prepared by electrophoretic co-deposition from organic suspension on a stainless steel substrate.  In this study, MWCNTs was incorporated to the coating because of their long structure and their capability to be functionalized by different inorganic groups on the surface. FTIR spectroscopy showed the existence of...

This paper studies the initiation of cohesive cracks in the thermal shock problem through a variational analysis. A two-dimensional semi-infinite slab with an imposed temperature drop on its free surface is considered. Assuming that cracks are periodically distributed and orthogonal to the surface, at short times we show that the optimum is a distribution of infinitely close cohesive cracks. Th...

This paper studies the initiation of cohesive cracks in the thermal shock problem through a variational analysis. A two-dimensional semi-infinite slab with an imposed temperature drop on its free surface is considered. Assuming that cracks are periodically distributed and orthogonal to the surface, at short times we show that the optimum is a distribution of infinitely close cohesive cracks. Th...

Corrosion surface damage in the form of pitting and micro-cracks is observed in many metals. Cracks usually initiate from the pits and grow under cyclic stresses and eventually lead to material failure. An image analysis based on wavelet transforms and fractals was used to study the corrosion morphology of nickel aluminum bronze metal under varying corrosion conditions and applied stresses. Ima...

In this study, enamel micro-cracks produced around composite restorations were observed on surfaces and vertical sections, using a stereomicroscope and a scanning electron microscope (SEM). The effects of various clinical factors, i.e. the curing system, the marginal form and the polishing period after filling, on the incidence of marginal enamel micro-cracks were examined. Enamel micro-cracks ...