protein memories are novel technologies which use the hidden abilities of bacteria proteins and biological molecules in order to the electronic processes. four decades before baceriorhdopsin ( br) protein was extracted from the membrane of halobacerinum salina rum found in high salt water depositions after its original discovery in 1967. in this study, for immobilizing the protein a film has be...

in this study, silver nanoparticles were synthesized by chemical reduction method at different concentrations of ag colloid in the range of 500-16000 ppm. nanoparticles were deposited by spin coating method on pre-etched glass and si substrates. structural, optical and electrical properties of the samples were studied using scanning electron microscopy equipped with edax, uv-vis spectrophotomet...

In this study, the spin coating of template-assisted method is used to synthesize poly[2,7-(9,9-dioctylfluorene)-alt-4,7-bis(thiophen-2-yl)benzo-2,1,3-thiadiazole] (PFO-DBT) nanorod bundles. The morphological, structural, and optical properties of PFO-DBT nanorod bundles are enhanced by varying the spin coating rate (100, 500, and 1,000 rpm) of the common spin coater. The denser morphological d...

Immobilised titanium dioxide (TiO2) in membrane structures has recently become attractive. This is due to the elimination of the separation step after the process of photocatalytic degradation. The efficiency of the TiO2 surface area exposed to UV light as the main important parameter needs to be considered. The immobilisation of TiO2 nanoparticles in the polyvinylidene fluoride (PVDF) membrane...

Polymer bulk hetero-junction solar cells of poly(3-hexylthiophene) (P3HT) donor and (6,6)-phenyl-C61-butyric acid methyl ester (PCBM) acceptor are fabricated by blade coating in toluene solution. Desired donor–acceptor self-organization is achieved without the slow drying process and high boiling point solvent. Power conversion efficiency is 3.8%, much higher than the 2.6% obtained by spin coat...

We report on the fabrication and characterization of thick UV-patternable hybrid sol-gel films by spin coating using a modified sol-gel process. Thick coating of 25 microns with crack-free surface can be produced by one spin coating step. Thick layers of more than 100 μm can be obtained with a multi-coating process. Characterization using different techniques including optical microscope and at...

During spincoating, the centrifugal force of the substrate spinning with several 1.000 rounds per minute (rpm) distributes few ml of resist over the substrate. Advantages: The high resist film thickness homogeneity as well as the short coating times make spincoating the most-applied coating technique at least in microelectronics. The fact that the coated resist already lost a significant amount...

We have developed a high-purity sol-gel coating for the interior surface of glass cells used for polarizing He by spin-exchange optical pumping. The coating is designed to minimize spin relaxation due to wall collisions. A longitudinal spin-relaxation time T1 in a sol-gel coated Pyrex cell of 34468 h was achieved, the longest T1 we have ever recorded for a gaseous sample. Repeated trials indica...

The phosphorus barrier layers at the doping procedure of silicon wafers were fabricated using a spin-coating method with a mixture of silica-sol and tetramethylammonium hydroxide, which can be formed at the rear surface prior to the front phosphorus spin-on-demand (SOD) diffusion and directly annealed simultaneously with the front phosphorus layer. The optimization of coating thickness was obta...