the accumulative roll bonding process is used as a severe plastic deformation technique to produce aluminum composite sheets with ultra fine structure. in this study the effect of simultaneous use mg and sic particles as reinforcements, on the tensile properties of the al-mg-sic hybrid compositeis studied. the al-mg-sic hybrid composites with different amounts of mg and sic contents were fabric...

abstract: in this study, al 2 o 3 –sic nanocomposites have been fabricated by mixing of alumina powder containing 0.05% weight magnesium oxide and silicon carbide nano powders, followed by hot pressing at 1650 0 c. the mechanical properties of al 2 o 3 -sic nanocomposites containing different volume fraction (2.5, 5, 7.5, 10 and 15%) of nano scale sic particles were investigated and compared wi...

Mono dispersed nano SiC particles with spherical morphology were synthesized in this project by hydrolysis and condensation mechanism during sol gel processing. pH, temperature and precursor’s ratio considered as the main parameters which could influence particles size. According to DLS test results, the smallest size of particles in the sol (<5nm) was obtained at pH<4. It can be observed from ...

Aluminum Matrix composites (AMCs) are light weight, high-strength materials with potential application in areas such as automobile, aerospace, defence, engineering and other industries. AMCs are projected to significantly reduce the overall weight of the vehicles and aircraft while maintaining satisfactory structural strength. Reinforcement of micron or nano-sized range particles with aluminium...

Aluminium base alloy (Al-Cu-Si) was reinforced with silicon carbide (SiC) particles, in various percentage compositions from 0-20 wt%. Silicon carbide particle size of 20µm was selected. The molten slurry of SiC reinforced base aluminium metal was casted through green and dry sand casting methods and solidification process was carried out under ambient conditions. A selected population...

Composites based on two aluminium alloys (A536 and 6061) reinforced with 10% or 20% volume fraction of SiC particles were produced by gravity casting and a novel two-step mixing method was applied successfully to improve the wettability and distribution of the particles. The SiC particles were observed to be located predominantly in the interdendrit ic regions, and a thermal lag model is propos...

in this research, using pyrolysis of phenolic resin in the presence of silicon particles, the sic ceramic composite is formed. the samples were prepared by introducing 30, 35, 40, 45 and 50 wt% of si particles to the phenolic resin. the samples were cured at 180°c then carbonized at 1100°c. the final carbonized c/si composites are hot-pressed at 1500°c in inert atmosphere, which is more than th...

We report on the residual stresses in amorphous shape memory polymers reinforced with SiC particles. After 50% compression of the composite material at 25 °C, the SiC particles exhibit a compressive stress, which is almost completely released during heated recovery at 120 °C. The residual stresses in SiC hexagonal (6H) phase were estimated through the average change of the unit-cell volume. Lat...