نتایج جستجو برای: Short fatigue crack

تعداد نتایج: 523276  

Journal: :international journal of iron & steel society of iran 2015
a. abyazi a. r. ebrahimi

microalloyed s355n steel plates are extensively used in bridge and high-rise building structures. one ofthe factors affecting the mechanical properties is the size and morphology of inclusions. in this research,microalloyed s355n steel plates with different sizes of inclusions were examined. one contained longmanganese sulfide inclusions (li material) and the other had short ones (si material)....

1998

In the short crack regime of the fatigue process, grain boundaries in steels are barriers against crack growth. In this paper, we use: (1) a method involving crack density; and (2) a method of dimensional analysis, to evaluate the effects of grain size and grain-boundary resistance on short crack behaviour and fatigue life. The results show that the fatigue life increases with a decrease in gra...

2004
J. J. Kruzic R. M. Cannon R. O. Ritchie

The role of grain bridging in affecting the initial rising portion of the R-curve and the transient, non-steady-state behavior of short cracks during (cyclic) fatigue-crack propagation has been quantitatively examined in a 99.5% pure alumina. Fatigue-crack growth properties for both long and short ( af < 2 mm) cracks emanating from machined notches (root radius, 15–150 m) were investigated, whe...

2016
Chuan Yang Wenchen Xu Bin Guo Debin Shan Jian Zhang

In order to investigate the methods to heal fatigue cracks in metals, tubular specimens of 1045 steel with axial and radial fatigue cracks were treated under the eddy current. The optical microscope was employed to examine the change of fatigue cracks of specimens before and after the eddy current treatment. The results show that the fatigue cracks along the axial direction of the specimen coul...

2009
P. A. S. Reed

An assessment of the effects of microstructure on room temperature fatigue crack initiation and short crack propagation in a Ni-base superalloy is presented. The assessment was carried out on microstructural variants of U720Li, including as-received U720Li, U720Li-LG (large grain variant) and U720Li-LP (large intragranular coherent γ′ variant). Fatigue tests were carried out at room temperature...

2015
S. Fouvry K. J. Kubiak

Fretting fatigue induced by combined localized cyclic contact motion and external bulk fatigue loadings may result in premature and dramatic failure of the contacting components. Depending on fretting and fatigue loading conditions, crack nucleation and possibly crack propagation can be activated. This paper proposes a procedure for estimating these two damage thresholds. The crack nucleation b...

2015
S. Fouvry K. Kubiak

Fretting fatigue induced by combined localized cyclic contact motion and external bulk fatigue loadings may result in premature and dramatic failure of the contacting components. Depending on fretting and fatigue loading conditions, crack nucleation and possibly crack propagation can be activated. This paper proposes a procedure for estimating these two damage thresholds. The crack nucleation b...

2016
K. Kubiak

Fretting fatigue induced by combined localized cyclic contact motion and external bulk fatigue loadings may result in premature and dramatic failure of the contacting components. Depending on fretting and fatigue loading conditions, crack nucleation and possibly crack propagation can be activated. This paper proposes a procedure for estimating these two damage thresholds. The crack nucleation b...

2006
T. Connolley P. A. S. Reed M. J. Starink

The natural initiation and growth of short cracks in Inconel 718 U-notch specimens has been studied at 600C in air. U notches were introduced through broaching, and hardness traces and optical microscopy on cross sections through the U notch broaching showed that the broaching process had introduced a deformed, work hardened layer. Fatigue tests were conducted under load control using a 1-1-1-1...

2000
J. P. Campbell R. O. Ritchie

Mixed-mode, high-cycle fatigue-crack growth thresholds are reported for through-thickness cracks (large compared to microstructural dimensions) in a Ti±6Al±4V turbine blade alloy with a bimodal microstructure. Speci®cally, the e€ect of combined mode I and mode II loading, over a range of phase angles b ˆ tanÿ1…DKII=DKI† from 0° to 82° …DKII=DKI 0±7), is examined for load ratios (ratio of minimu...