The objective of the present study was to develop a practical method to prepare a stable dispersion of TiO2 nanoparticles for biological studies. To address this matter a variety of different approaches for suspension of nanoparticles were conducted. TiO2 (rutile/anatase) dispersions were prepared in distilled water following by treated with different ultrasound energies and various dispersion ...

The paper deals with application of three nanomaterial systems: undoped TiO2, chromium-doped TiO2:Cr and TiO2-SnO2 synthesized by flame spray synthesis (FSS) technique for hydrogen sensing. The emphasis is put on the role of anatase and rutile polymorphic forms of TiO2 in enhancing sensitivity towards reducing gases. Anatase-to-rutile transformation is achieved by annealing of undoped TiO2 in a...

In general, anatase TiO2 exhibits higher photocatalytic activities than rutile TiO2. However, the reasons for the differences in photocatalytic activity between anatase and rutile are still being debated. In this work, the band structure, density of states, and effective mass of photogenerated charge carriers for anatase, rutile and brookite TiO2 are investigated by the first-principle density ...

In this study, the commercial TiO2 nanopowder and micropowder of anatase phase and rutile phase have been characterized by x-ray diffraction (XRD) and transmission electron microscopy (TEM). XRD patterns of nano-TiO2 in rutile and anatase phases exhibit broad peaks whereas both phases of micro-TiO2 demonstrate very sharp peaks. TEM images show that the grain size of TiO2 micropowders and TiO2 n...

The SrTiO3 modified rutile TiO2 composite nanofibers were synthesized by a simple electrospinning technique. The result of XRD, SEM and TEM indicate that the SrTiO3/TiO2 heterojuction has been prepared successfully. Compared with the TiO2 and SrTiO3, the photocatalytic activity of the SrTiO3/TiO2 (rutile) for the degradation of methyl orange exhibits an obvious enhancement under UV illumination...

TiO2 with tailored anatase/rutile composition has been prepared from the supercritical antisolvent (SAS) precipitation of a range of titanium alkoxides. The calcination of the SAS TiO2 was monitored by in situ powder X-ray diffraction to determine the optimal calcination conditions for the formation of a mixed anatse/rutile phase TiO2. The SAS precipitated material calcined at 450 °C produced a...

Absorption spectra of anatase and rutile TiO2 in the 150-300 nm region before and after the deposition of Pt nanoparticles were measured. For anatase TiO2, the spectral intensity in the longer wavelength region decreased (>∼210 nm), while that in the shorter wavelength region increased (<∼210 nm). In particular, spectral band intensity in the far-ultraviolet (FUV) region (∼160 nm) was increased...

For TiO2 photocatalysts, recombination of photoexcited electrons and holes would occur in crystalline defects such as oxygen vacancies, Ti ions, and surface states. Therefore, it is believed that the density of crystalline defects should be decreased to improve the photocatalytic activity of TiO2 particles. Contrary to this common knowledge, the introduction of crystalline defects by hydrogen r...

In this study, we focused on the origin on the selective deposition of rutile and anatase TiO2 thin films during the sputtering process. The observation on microstructural evolution of the TiO2 films by transmission electron microscopy revealed the coexistence of rutile and anatase TiO2 phases in the initial stage under the preferential growth conditions for the anatase TiO2; the observations f...

To test the hypothesis that wood coated with rutile TiO2 nanostructures can undergo degradation because of the photocatalytic activity of TiO2, three sets of wood specimens were aged at an accelerated rate. These three sets consisted of blank wood (BW), HDTMOS/MTMOS-coated wood (WHM), and TiO2/HDTMOS/MTMOS-coated wood (WTHM). After exposure to 155-h UV irradiation, the wettability of WTHM chang...